Thermoelectric Properties of Undoped and Doped (Ti0.75Sn0.25)O2

被引:15
作者
Dynys, Frederick W. [1 ]
Berger, Marie-Helene [2 ]
Sehirlioglu, Alp [3 ]
机构
[1] NASA, Glenn Res Ctr, Cleveland, OH 44135 USA
[2] MINES ParisTech, Ctr Mat, CNRS, UMR 7633, F-91003 Evry, France
[3] Case Western Reserve Univ, Dept Mat Sci & Engn, Cleveland, OH 44106 USA
关键词
TIO2-SNO2; SYSTEM; SOLID-SOLUTIONS; ELECTRICAL-PROPERTIES; SEEBECK COEFFICIENT; ALIOVALENT DOPANTS; DECOMPOSITION; TRANSPORT; POWER; PRECIPITATION; CERAMICS;
D O I
10.1111/j.1551-2916.2011.04794.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Thermoelectric properties of undoped and doped (Ti0.75Sn0.25)O-2 were investigated for high-temperature thermoelectric conversion application. Nano-composites were formed by annealing above 1000 degrees C. Outside the spinodal dome, ilmenite-type SnTiO3 precipitated from the rutile structure. Thermoelectric properties were measured in the temperature range from room temperature to 1000 degrees C. (Ti0.75Sn0.25)O-2 was doped with both acceptor and donor dopants. Both undoped and doped (Ti0.75Sn0.25)O-2 exhibit n-type electrical behavior independent of the type of the dopant. The electrical conductivity was enhanced three orders of magnitude by donor doping with Nb2O5 or Ta2O5; achieving a maximum of 546 S/m at 850 degrees C. The increase in electrical conductivity was accompanied by reduction of the absolute Seebeck coefficient. Seebeck coefficient reduction of -600 mu V/K was observed between undoped and 4% Ta2O5 doped samples. The solid solution and doping reduced the thermal conductivity to <4 W/mK, far below the parent materials TiO2 and SnO2. Lattice thermal conductivity decreased with increasing temperature, achieving 1.9 W/mK at 900 degrees C for 4% Ta2O5 doping. No further reduction in thermal conductivity was observed in annealed samples containing nano-sized SnTiO3 precipitates. Dimensionless figure of merit (ZT) attained was <0.1.
引用
收藏
页码:619 / 626
页数:8
相关论文
共 26 条
[1]  
[Anonymous], 2000, DEFECT CHEM MET OXID
[2]  
BANFIELD JF, 1991, AM MINERAL, V76, P113
[3]  
BROOKS MH, 783761311963 US NAV
[4]   Sintering and mass transport features of (Sn,Ti)O2 polycrystalline ceramics [J].
Bueno, PR ;
Leite, ER ;
Bulhoes, LOS ;
Longo, E ;
Paiva-Santos, CO .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2003, 23 (06) :887-896
[5]  
Bueno PR, 2002, J AM CERAM SOC, V85, P282, DOI 10.1111/j.1151-2916.2002.tb00084.x
[6]   Grain size-dependent electrical properties of rutile (TiO2) [J].
Demetry, C ;
Shi, XL .
SOLID STATE IONICS, 1999, 118 (3-4) :271-279
[7]   RE-EXAMINATION OF SYSTEM TIO2-SNO2 [J].
GARCIA, D ;
SPEIDEL, D .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1972, 55 (06) :322-&
[8]  
Heikes R.R., 1961, Thermoelectricity: Science and Engineering (Interscience)
[9]   The influence of sintering process and atmosphere on the non-ohmic properties of SnO2 based varistor [J].
Leite, ER ;
Nascimento, AM ;
Bueno, PR ;
Longo, E ;
Varela, JA .
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 1999, 10 (04) :321-327
[10]   Critical thickness for giant thermoelectric Seebeck coefficient of 2DEG confined in SrTiO3/SrTi0.8Nb0.2O3 superlattices [J].
Ohta, Hiromichi ;
Mune, Yoriko ;
Koumoto, Kunihito ;
Mizoguchi, Teruyasu ;
Ikuhara, Yuichi .
THIN SOLID FILMS, 2008, 516 (17) :5916-5920