High-Temperature Corrosion of a Nickel Alloy

被引：0

作者：

Poilov, V. Z. ^{[1
]}

Kazantsev, A. L. ^{[1
]}

Skovorodnikov, P., V ^{[1
]}

Saulin, D., V ^{[1
]}

Uglev, N. P. ^{[1
]}

Puzanov, A., I ^{[2
]}

机构：

[1] Perm Natl Res Polytech Univ, Perm 614990, Russia

[2] AO UEC Aviadvigatel, Perm 614010, Russia

来源：

INORGANIC MATERIALS-APPLIED RESEARCH | 2022年 / 13卷 / 01期

关键词：

high-temperature corrosion; nickel superalloy; oxide film; corrosive; sulfur dioxide; HOT CORROSION; BEHAVIOR; OXIDATION; CMSX-4;

D O I：

10.1134/S2075113322010324

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

High-temperature corrosion of nickel superalloy VZhM4-VI is studied in environments containing different concentrations of corrosive SO2 (0.01, 1.00, and 10.00%). The corrosion process results in the formation of a mixture of different oxides on the alloy surface. As the SO2 content of the corrosive environment is increased, the metal is affected by progressively more severe corrosion.

引用

页码：39 / 43

页数：5

共 14 条

[1] Oxidation and Hot Corrosion Behaviors of Service-Exposed and Heat-Treated Gas Turbine Vanes Made of IN939 Alloy [J].

Abedini, M. ;

Jahangiri, M. R. ;

Karimi, P. .

OXIDATION OF METALS, 2018, 90 (3-4) :469-484

[2]

Birks N, 2006, INTRODUCTION TO THE HIGH-TEMPERATURE OXIDATION OF METALS, 2ND EDITION, P1, DOI 10.1017/CBO9781139163903

[3] Interaction of Ta and Cr on Type-I hot corrosion resistance of single crystal Ni-base superalloys [J].

Chang, J. X. ;

Wang, D. ;

Zhang, G. ;

Lou, L. H. ;

Zhang, J. .

CORROSION SCIENCE, 2017, 117 :35-42

[4] Evaluating the Hot Corrosion Behavior of High-Temperature Alloys for Gas Turbine Engine Components [J].

Deodeshmukh, V. P. .

JOM, 2015, 67 (11) :2608-2614

[5] Hot corrosion behavior of Ni based Inconel 617 and Inconel 738 superalloys [J].

El-Awadi, G. A. ;

Abdel-Samad, S. ;

Elshazly, Ezzat S. .

APPLIED SURFACE SCIENCE, 2016, 378 :224-230

[6] OXIDE SCALE FORMATION ON SELECTED CANDIDATE COMBUSTOR ALLOYS IN SIMULATED GAS-TURBINE ENVIRONMENTS [J].

GANESAN, P ;

SMITH, GD .

JOURNAL OF MATERIALS ENGINEERING, 1988, 9 (04) :337-343

[7]

Gishvarov A.S., MEZHVUZOVSKII SBORNI, P157

[8] Correlations between the kinetics and the mechanisms of hot corrosion of pure nickel at 700 °C [J].

Gregoire, Benjamin ;

Montero, Xabier ;

Galetz, Mathias C. ;

Bonnet, Gilles ;

Pedraza, Fernando .

CORROSION SCIENCE, 2019, 155 :134-145

[9] Effect of SO2 Addition on Air Oxidation Behavior of CM247 and CMSX-4 at 1050°C [J].

Jalowicka, A. ;

Nowak, W. J. ;

Naumenko, D. ;

Quadakkers, W. J. .

JOM, 2016, 68 (11) :2776-2785

[10] High Temperature Corrosion of Ni-Based Alloys SCA425+and IN792 [J].

Lai, H. ;

Cao, Y. ;

Viklund, P. ;

Karlsson, F. ;

Johansson, L. -G. ;

Stiller, K. .

OXIDATION OF METALS, 2013, 80 (5-6) :505-516

← 1 2 →