Two-dimensional correlation analysis of continuous online in situ ATR-FTIR on the adsorption of butyl xanthate at the surface of α-PbO

The adsorption behavior of butyl xanthate on the surface of lead oxide was investigated using continuous online in situ attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy technique and two dimensional (2D) correlation analysis. The adsorbed layer studied was prepared by coating alpha-PbO particles onto the surfaces of the ZnSe crystal. The appearance of spectral peaks at 1203 cm(-1), 1033 cm(-1) and their red shift indicated the formation and aggregation of xanthate at the surface of alpha-PbO. According to IR intensity changes after rinsing with deionized water and a NaOH solution, the adsorption was proved to be a chemisorption type. The competition between xanthate and OH- for the surfaces leads to desorption of xanthate at higher pH. The technique of 2D correlation ATR-FTIR spectroscopy was used to evaluate the changing order of spectral intensities in the adsorption process, and the results indicated that xanthate micelles were formed at the surfaces. The adsorption kinetics of butyl xanthate was found to be a pseudo-second-order reaction model and the adsorption capacity of butyl xanthate at alpha-PbO was as high as 281 mg g(-1) after 150 min. (C) 2014 Zhong-Xi Sun. Published by Elsevier B.V. on behalf of Chinese Chemical Society and Institute of Materia Medica, Chinese Academy of Medical Sciences. All rights reserved.