Microstructure and phase transformation of as-cast and annealed Mg-4Zn-1Y alloy containing quasi-crystal phase

被引：14

作者：

Yang, Yang ^{[1
]}

Zhang, Kui ^{[1
]}

Li, Xing-Gang ^{[1
]}

Li, Yong-Jun ^{[1
]}

Ma, Ming-Long ^{[1
]}

Shi, Guo-Liang ^{[1
]}

Yuan, Jia-Wei ^{[1
]}

机构：

[1] Gen Res Inst Nonferrous Met, State Key Lab Fabricat & Proc Nonferrous Met, Beijing 100012, Peoples R China

来源：

RARE METALS | 2015年 / 34卷 / 04期

基金：

中国国家自然科学基金;

关键词：

Mg-Zn-Y alloy; Heat treatment; Microstructure; Phase transformation; Icosahedral quasi-crystal; ZN-Y ALLOYS; MECHANICAL-PROPERTIES; EXTRUSION; NACL;

D O I：

10.1007/s12598-014-0443-8

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

By means of optical microscope (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses, the microstructures of as-cast and heat-treated Mg-4Zn-1Y (wt%) alloy containing quasi-crystal phase were studied. The microstructure of the as-cast alloy consists of alpha-Mg solid solution grains, intermetallic particles and eutectic phases (W-phase and I-phase), and huge grains with serious dendritic segregation are clearly observed. After heat treatment, phase transformation and dissolution occur in the alloy and many phases remain. When the alloy was treated above 410 A degrees C, the eutectic phases transform into spherical shape as the I-phase turns to W-phase. After heat treatment for long time, the alloy is over burnt and the W-phase decomposes to Mg-Y binary phase.

引用

页码：239 / 244

页数：6

共 21 条

[1] Texture and stretch formability of rolled Mg-Zn-RE(Y, Ce, and Gd) alloys at room temperature [J].

Cai, Zheng-Xu ;

Jiang, Hai-Tao ;

Tang, Di ;

Ma, Zhao ;

Kang, Qiang .

RARE METALS, 2013, 32 (05) :441-447

[2]

[郭永春 Guo Yongchun], 2014, [稀有金属, Chinese Journal of Rare Metals], V38, P603

[3] The effect of nanoquasicrystals on mechanical properties of as-extruded Mg-Zn-Gd alloy [J].

Huang, Hua ;

Kato, Hidemi ;

Chen, Chunlin ;

Wang, Zhongchang ;

Yuan, Guangyin .

MATERIALS LETTERS, 2012, 79 :281-283

[4] The corrosion behaviors of Mg-7Gd-5Y-1Nd-0.5Zr alloy under (NH4)(2)SO4, NaCl and Ca(NO3)(2) salts spray condition [J].

Jiang, Quantong ;

Zhang, Kui ;

Li, Xinggang ;

Li, Yongjun ;

Ma, Minglong ;

Shi, Guoliang ;

Yuan, Jiawei .

JOURNAL OF MAGNESIUM AND ALLOYS, 2013, 1 (03) :230-234

[5] Stable icosahedral phase in Mg-Zn-Gd alloy [J].

Liu, Yong ;

Yuan, Guangyin ;

Lu, Chen ;

Ding, Wenjiang .

SCRIPTA MATERIALIA, 2006, 55 (10) :919-922

[6] Effect of mole ratio of Y to Zn on phase constituent of Mg-Zn-Zr-Y alloys [J].

Luo Su-qin ;

Tang Ai-tao ;

Pan Fu-sheng ;

Song Kai ;

Wang Wei-qing .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2011, 21 (04) :795-800

[7] Thermodynamic stability of Mg-Y-Z long-period stacking ordered structures [J].

Saal, James E. ;

Wolverton, C. .

SCRIPTA MATERIALIA, 2012, 67 (10) :798-801

[8] Thermodynamic modelling of the Y-Zn and Mg-Zn-Y systems [J].

Shao, G. ;

Varsani, V. ;

Fan, Z. .

CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2006, 30 (03) :286-295

[9] Microstructure of ZM6 magnesium alloy with different Nd content [J].

Shi, Weng-Yong ;

Ma, Yan .

RARE METALS, 2013, 32 (03) :234-240

[10] Microstructure and strength of quasicrystal containing extruded Mg-Zn-Y alloys for elevated temperature application [J].

Singh, A ;

Watanabe, M ;

Kato, A ;

Tsai, AP .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 385 (1-2) :382-396

← 1 2 3 →