Effect of Rectorite and Its Organic Modification on Properties of Bitumen

被引：15

作者：

Zhang, Henglong ^{[1
]}

Zhu, Chongzheng ^{[1
]}

Yan, Kezhen ^{[1
]}

Yu, Jianying ^{[2
]}

机构：

[1] Hunan Univ, Coll Civil Engn, Changsha 410082, Hunan, Peoples R China

[2] Wuhan Univ Technol, State Key Lab Silicate Mat Architectures, Wuhan 430070, Peoples R China

来源：

JOURNAL OF MATERIALS IN CIVIL ENGINEERING | 2015年 / 27卷 / 08期

基金：

中国国家自然科学基金;

关键词：

Bitumen; Rectorite; Organic modification; Microstructure; Aging resistance; MONTMORILLONITE; MORPHOLOGY; CHEMISTRY; BEHAVIOR; RUBBER;

D O I：

10.1061/(ASCE)MT.1943-5533.0000972

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Two organic rectorites (ORECs) were prepared by using cetyltrimethyl ammonium bromide (CTAB) and octadecyl dimethyl benzyl ammonium chloride (ODBA) as organic modifiers to modify the rectorites. Rectorite and OREC modified bitumens were prepared by melt blending. Microstructures of the modified bitumens were characterized by X-ray diffraction (XRD). The effect of rectorite (REC) and its organic modification on the physical and aging properties of bitumen was investigated. X-ray diffraction results show that REC and ODBA-REC modified bitumens form the intercalated nanostructure, whereas CTAB-REC modified bitumen forms an exfoliated nanostructure. Compared with RECs, ORECs show the better compatibility with the bitumen as well as the higher improvement in softening point, viscosity, and aging resistance of the bitumen. The CTAB-REC modified bitumen shows lower viscosity aging index values and softening point increment in comparison with the ODBA-REC modified bitumen, indicating its good aging resistance. (C) 2014 American Society of Civil Engineers.

引用

页数：5

共 29 条

[1] Asphalt modified by SBS triblock copolymer: Structures and properties [J].

Adedeji, A ;

Grunfelder, T ;

Bates, FS ;

Macosko, CW ;

StroupGardiner, M ;

Newcomb, DE .

POLYMER ENGINEERING AND SCIENCE, 1996, 36 (12) :1707-1723

[2]

[Anonymous], 2003, 0740 SHT

[3]

[Anonymous], 2007, D11317 ASTM, DOI DOI 10.1520/D0113-17

[4]

[Anonymous], 2012, ASTM D36

[5]

[Anonymous], 2009, Standard Test Method for Effects of Heat and Air on Asphaltic Materials (Thin-Film Oven Test)

[6]

ASTM, 2012, ASTM D4402

[7]

ASTM, 2008, D6521 ASTM

[8]

ASTM, 2013, ASTM D5 .

[9]

[陈繁华 CHEN Fanhua], 2007, [武汉理工大学学报, Journal of wuhan university of technology], V29, P35

[10] Influence of the Type of Binder and Crumb Rubber on the Creep and Recovery of Crumb Rubber Modified Bitumen [J].

Divya, P. S. ;

Gideon, C. S. ;

Krishnan, J. Murali .

JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2013, 25 (04) :438-449

← 1 2 3 →