Alumina nanoparticle modified phenol-formaldehyde resin as a wood adhesive

被引：34

作者：

Zhang, Rong ^{[1
]}

Jin, Xiaobei ^{[1
]}

Wen, Xuwen ^{[1
]}

Chen, Qi ^{[1
]}

Qin, Daochun ^{[1
]}

机构：

[1] Int Ctr Bamboo & Rattan, Wangjing Area, 8 Futongdongdajie, Beijing, Peoples R China

来源：

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES | 2018年 / 81卷

关键词：

Phenol-formaldehyde; alumina nanoparticles; plywood; bonding strength; RESOL RESINS; CURE; COMPOSITES; OXIDE;

D O I：

10.1016/j.ijadhadh.2017.11.013

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Phenol-formaldehyde resin was synthesized and modified by alumina nanoparticles (ANPs). The crystal form of the ANPs was characterized by X-ray diffraction (XRD), and differential scanning calorimetry (DSC) was used for thermal analysis of the resin. In addition, the resin was applied in plywood manufacture, and the curing time as well as the bonding strength was measured. The results showed, with an appropriate doping amount of ANPs, both the curing rate and the bonding strength increased significantly. The modified resin showed extensive application prospects in the wood construction industry.

引用

页码：79 / 82

页数：4

共 50 条

[1] Relevance between Cassava Starch Liquefied by Phenol and Modification of Phenol-Formaldehyde Resin Wood Adhesive [J].

Liu, Jinming ;

Fang, Jianlin ;

Xie, Enjun ;

Gan, Weixing .

POLYMERS, 2022, 14 (09)

[2] Curing of phenol-formaldehyde resin mixed with wood preservatives [J].

Miyazaki, Junko ;

Furuta, Naoyuki ;

Miyauchi, Teruhisa .

JOURNAL OF APPLIED POLYMER SCIENCE, 2013, 128 (05) :2896-2901

[3] CHARACTERIZATION OF WOOD FIBERS MODIFIED BY PHENOL-FORMALDEHYDE [J].

KAMDEM, DP ;

RIEDL, B .

COLLOID AND POLYMER SCIENCE, 1991, 269 (06) :595-603

[4] Preparation and characterization of a novel environmentally friendly phenol-formaldehyde adhesive modified with tannin and urea [J].

Li, Cheng ;

Zhang, Jizhi ;

Yi, Zhao ;

Yang, Hua ;

Zhao, Bin ;

Zhang, Wei ;

Li, Jianzhang .

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2016, 66 :26-32

[5] Fatigue behavior of beech and pine wood modified with low molecular weight phenol-formaldehyde resin [J].

Pecnik, Jaka Gasper ;

Kutnar, Andreja ;

Militz, Holger ;

Schwarzkopf, Matthew ;

Schwager, Hannes .

HOLZFORSCHUNG, 2021, 75 (01) :37-47

[6] Characterization and Adhesive Performance of Phenol-Formaldehyde Resol Resin Reinforced with Carbon Nanotubes [J].

Ciritcioglu, Hasan Huseyin ;

Ozbay, Gunay .

BIORESOURCES, 2022, 17 (03) :4781-4792

[7] Study on Physical and Mechanical Properties of Poplar Modified by Phenol-formaldehyde Resin [J].

CHAI Yubo LIU Huanrong LIU Junliang LI Longzhe TANG Deguo Research Institute of Wood Industry Chinese Academy of Forestry Beijing PRChina Construction Bureau of Yanbian Korean Autonomous Prefecture Yanji PRChina Forestry Bureau of Wangqing County Wangqing PRChina .

Chinese Forestry Science and Technology, 2008, (01) :82-87

[8] Synthesis and Characterization of an Environmentally Friendly Phenol-Formaldehyde Resin Modified with Waste Plant Protein [J].

Li, Hanyin ;

Wang, Sen ;

Zhang, Xiang ;

Wu, Hao ;

Wang, Yujie ;

Zhou, Na ;

Zhao, Zijie ;

Wang, Chao ;

Zhang, Xiaofan ;

Wang, Xian ;

Li, Cheng .

POLYMERS, 2023, 15 (13)

[9] A dynamic mechanical analysis method for predicting the curing behavior of phenol-formaldehyde resin adhesive [J].

Lei, Hong ;

Frazier, Charles E. .

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2015, 29 (10) :981-990

[10] Preparation and Characterization of a Phenol-formaldehyde Resin Adhesive Obtained from Bio-ethanol Production Residue [J].

Qiao, Wei ;

Li, Shujun ;

Xu, Fengying .

POLYMERS & POLYMER COMPOSITES, 2016, 24 (02) :99-105

← 1 2 3 4 5 →