Powder X-ray Diffraction Analysis of Lime-Phase Solid Solution in Converter Slag

被引:10
作者
Nishinohara, Ippei [1 ]
Kase, Naoki [1 ]
Maruoka, Hirokazu [1 ]
Hirai, Shoji [1 ]
Eba, Hiromi [1 ]
机构
[1] Tokyo City Univ, Setagaya Ku, Tokyo 1588557, Japan
关键词
converter slag; lime phase; crystallized lime; solid solution; aging; hydration; X-ray diffraction; SYSTEM;
D O I
10.2355/isijinternational.55.616
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
X-ray diffraction analysis of a converter slag was performed by focusing on the lime-phase solid solution. Solid solutions of Ca1-xFexO and Ca1-xMnxO (0 < x < 1) were prepared by mechanochemical processing or high-temperature solid-state reaction, and the relationships between solid solubility x and lattice parameters were determined. Crystallized lime could be distinguished from undissolved lime by the shift of the diffraction angle associated with the formation of the solid solution. The effect of slag aging treatment with water vapor was examined by comparing the solid solubility x and the amount of lime phase in the aged and non-aged slags. It was confirmed that x affects the hydration behavior of the lime phase and that crystallized lime with high x tends to remain unchanged even after aging. Moreover, about two-thirds of the lime phase was confirmed to have been converted by hydration as a result of the aging process.
引用
收藏
页码:616 / 622
页数:7
相关论文
共 14 条
[1]  
ABBATTISTA F, 1975, REV INT HAUTES TEMP, V12, P337
[2]   DISCRETE VARIATIONAL X-ALPHA CLUSTER CALCULATIONS .1. APPLICATION TO METAL CLUSTERS [J].
ADACHI, H ;
TSUKADA, M ;
SATOKO, C .
JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN, 1978, 45 (03) :875-883
[3]  
[Anonymous], 2013, ENV MAT IR STEEL SLA
[4]   MECHANOCHEMISTRY OF INORGANIC SOLIDS [J].
BOLDYREV, VV .
THERMOCHIMICA ACTA, 1987, 110 :303-317
[5]  
Fujim H., 1970, TETSU TO HAGANE, V56, P830
[6]   Calorimetric study on hydration of CaO-based oxides [J].
Iguchi, Y ;
Narushima, T ;
Izumi, C .
JOURNAL OF ALLOYS AND COMPOUNDS, 2001, 321 (02) :276-281
[7]  
MacPherson D.R., 1937, Industrial and Engineering Chemistry Analytical Edition, V9, P451
[8]   THE EFFECTS OF PRESSURE AND TEMPERATURE ON NONSTOICHIOMETRIC WUSTITE, FEXO - THE IRON-RICH PHASE-BOUNDARY [J].
MCCAMMON, CA ;
LIU, LG .
PHYSICS AND CHEMISTRY OF MINERALS, 1984, 10 (03) :106-113
[9]  
Narita K., 1978, TETSU TO HAGANE, V64, P1558, DOI 10.2355/tetsutohagane1955.64.101558
[10]   SYSTEM CALCIUM OXIDE-IRON(2)-OXIDE AS BASIS FOR INVESTIGATIONS INTO LIME DISSOLUTION DURING STEELMAKING [J].
OBST, KH ;
STRADTMA.J .
ARCHIV FUR DAS EISENHUTTENWESEN, 1969, 40 (08) :615-&