Characteristics of nitrogen-doped p-ZnO thin films and ZnO/ZnSe p-n heterojunctions grown on a ZnSe substrate

被引:12
作者
Rogozin, I. V. [1 ]
Kotlyarevsky, M. B. [2 ]
机构
[1] Berdyansk State Univ, UA-71100 Berdyansk, Ukraine
[2] Acad Management & Technol, UA-71100 Berdyansk, Ukraine
关键词
D O I
10.1088/0268-1242/23/8/085008
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
We investigate p-type doping in ZnO prepared by the method of radical beam gettering epitaxy using NO gas as the oxygen source and nitrogen dopant. A narrow (0 0 2) peak is observed in the x-ray diffraction spectra, which indicates that the N-doped ZnO films are oriented along the c-axis. Secondary ion mass spectroscopy measurements demonstrate that N is incorporated into a ZnO film with a concentration of about 2.5 x 10(19) cm(-3). The hole concentration of the N-doped p-ZnO films was between 1.4 x 10(17) and 7.2 x 10(17) cm(-3), and the hole mobility was 0.9-1.2 cm(2) V-1 s(-1) as demonstrated by Hall-effect measurements. The emission peak of 3.312 eV is observed in the photoluminescence spectra at 4.2 K of N-doped p-ZnO films, probably neutral acceptor bound excitons and the band of 3.24 eV, connected with a donor-acceptor pair recombination. The activation energy of the nitrogen acceptor was obtained by the temperature-dependent Hall-effect measurement, and is about 145 meV. The p-n heterojunctions ZnO/ZnSe were grown on the n-type ZnSe substrate, and have a turn-on voltage of about 3.5 V.
引用
收藏
页数:5
相关论文
共 50 条
[31]   Conduction characteristics of N-Al codoping p-ZnO films by XPS [J].
Zhang, Zi-Cai ;
Yu, Wei ;
Zhang, Kun ;
Teng, Xiao-Yun ;
Fu, Guang-Sheng .
Rengong Jingti Xuebao/Journal of Synthetic Crystals, 2011, 40 (05) :1199-1202
[32]   Performance analysis of Schottky diodes based on Bi doped p-ZnO thin films [J].
Singh, Brijesh Kumar ;
Tripathi, Shweta .
SUPERLATTICES AND MICROSTRUCTURES, 2018, 120 :288-297
[33]   NH3 Sensing by p-ZnO Thin Films [J].
Balakrishnan, Lakshmi Narayanan ;
Gowrishankar, Subramaniam ;
Gopalakrishnan, Nammalvar .
IEEE SENSORS JOURNAL, 2013, 13 (06) :2055-2060
[34]   p-type ZnO films by codoping of nitrogen and aluminum and ZnO-based p-n homojunctions [J].
Lu, JG ;
Zhu, LP ;
Ye, ZZ ;
Zhuge, F ;
Zhao, BH ;
Huang, JY ;
Wang, L ;
Yuan, J .
JOURNAL OF CRYSTAL GROWTH, 2005, 283 (3-4) :413-417
[35]   Synthesis and characterisation of nitrogen-doped ZnO thin films [J].
Mekki, Abdelkrim ;
Tabet, Nouar ;
Hezam, Mahmoud .
International Journal of Nano and Biomaterials, 2009, 2 (1-5) :216-225
[36]   Junction properties of nitrogen-doped ZnO thin films [J].
Lu, J. G. ;
Fujita, S. ;
Kawaharamura, T. ;
Nishinaka, H. ;
Kamada, Y. .
PHYSICA STATUS SOLIDI C - CURRENT TOPICS IN SOLID STATE PHYSICS, VOL 5, NO 9, 2008, 5 (09) :3088-+
[37]   ZnSe nanowire/Si p-n heterojunctions: device construction and optoelectronic applications [J].
Zhang, Xiwei ;
Zhang, Xiujuan ;
Wang, Liu ;
Wu, Yiming ;
Wang, Yan ;
Gao, Peng ;
Han, Yuanyuan ;
Jie, Jiansheng .
NANOTECHNOLOGY, 2013, 24 (39)
[39]   Impurity effects in ZnO and nitrogen-doped ZnO thin films fabricated by MOCVD [J].
Li, XN ;
Asher, SE ;
Limpijumnong, S ;
Keyes, BM ;
Perkins, CL ;
Barnes, TM ;
Moutinho, HR ;
Luther, JM ;
Zhang, SB ;
Wei, SH ;
Coutts, TJ .
JOURNAL OF CRYSTAL GROWTH, 2006, 287 (01) :94-100
[40]   Characteristics of p-ZnO/n-GaN heterojunction photodetector [J].
Al-Zouhbi, Abla ;
Al-Din, Nasser Saad ;
Manasreh, M. Omar .
OPTICAL REVIEW, 2012, 19 (04) :235-237