Localized corrosion behavior of scratches on nickel-base Alloy 690TT

被引：46
|
作者：
Meng, Fanjiang [1 ]
Han, En-Hou [1 ]
Wang, Jianqiu [1 ]
Zhang, Zhiming [1 ]
Me, Wei [1 ]
机构：
[1] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
来源：
ELECTROCHIMICA ACTA | 2011年 / 56卷 / 04期
关键词：
Scratch; Localized corrosion; SECM; Crack initiation; Alloy; 690; SCANNING ELECTROCHEMICAL MICROSCOPY; OXIDATION; CRACKING; WATER;
D O I：
10.1016/j.electacta.2010.08.028
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Localized corrosion of scratched Alloy 690TT was studied using scanning electrochemical microscopy (SECM) in 10 wt.% NaOH solution and atomic force microscopy (AFM) after short-time oxidation tests in high temperature high pressure water at 250 degrees C. The results show that the scratches detected by SECM displayed more extensive electrochemical activity. The scratch groove and the whole deformed region caused by scratching as anode corresponded to the peak of tip current. The oxides formed in 250 degrees C high purity pressurized water nucleated preferentially at the scratch groove and grew faster than non-scratched surface. The nano-grained scratch groove has more electrochemical reactivity than mechanical twins at scratch banks. The intense localized corrosion could contribute to crack initiation at the bottom of scratch groove. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1781 / 1785
页数：5
相关论文
共 50 条
  • [31] Grain growth and intergranular carbide precipitation in nickel-base alloy 690
    Lim, YS
    Hwang, SS
    Suh, JH
    Kim, JS
    RECRYSTALLIZATION AND GRAIN GROWTH, VOLS 1 AND 2, 2001, : 389 - 394
  • [32] Lead-induced stress corrosion cracking (PbSCC) initiation in alloy 690TT in caustic environment
    Mazzei, G. B.
    Burke, M. G.
    Horner, D. A.
    Scenini, F.
    CORROSION SCIENCE, 2022, 206
  • [33] The effect of NaCl concentration on impact-sliding fretting corrosion behavior of Inconel 690TT heat transfer tubes
    Li, Yinghong
    Tan, Wei
    Pei, Wenjie
    Zhu, Guorui
    ANTI-CORROSION METHODS AND MATERIALS, 2024, 71 (05) : 464 - 481
  • [34] Characterization of Different Surface States and Its Effects on the Oxidation Behaviours of Alloy 690TT
    Zhang, Zhiming
    Wang, Jianqiu
    Han, En-Hou
    Ke, Wei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (04) : 353 - 361
  • [35] Prediction Model of Crack Growth Rate of Stress Corrosion for Nickel-Base 690 Alloy Based on KBRF Algorithm
    Mei Jinna
    Wang Peng
    Han Yaolei
    Cai Zhen
    Ti Wenxin
    Peng Qunjia
    Xue Fei
    RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (04) : 1304 - 1311
  • [36] Insights into the SCC crack tip of Alloy 690TT in caustic solution at high temperature
    Wang, X. Y.
    Li, Z. H.
    Bai, Y. K.
    Cao, X. Y.
    Liu, T. G.
    Lu, Y. H.
    Shoji, T.
    JOURNAL OF NUCLEAR MATERIALS, 2021, 553
  • [37] Effects of surface grinding for scratched alloy 690TT tube in PWR nuclear power plant: Microstructure and stress corrosion cracking
    Wu, Bin
    Ming, Hongliang
    Meng, Fanjiang
    Li, Yifeng
    He, Guangqing
    Wang, Jianqiu
    Han, En-Hou
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 113 : 229 - 245
  • [38] Effects of dissolved oxygen on partial slip fretting corrosion of Alloy 690TT in high temperature pure water
    Xin, Long
    Han, Yongming
    Ling, Ligong
    Lu, Yonghao
    Shoji, Tetsuo
    JOURNAL OF NUCLEAR MATERIALS, 2020, 542
  • [39] Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution
    Zhang, Zhiming
    Wang, Jianqiu
    Han, En-Hou
    Ke, Wei
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (09) : 785 - 792
  • [40] The role of material transfer in fretting wear behavior and mechanism of Alloy 690TT mated with Type 304 stainless steel
    Xin, Long
    Lu, Yonghao
    Shoji, Tetsuo
    MATERIALS CHARACTERIZATION, 2017, 130 : 250 - 259
12345