Localized corrosion behavior of scratches on nickel-base Alloy 690TT

被引：46
|
作者：
Meng, Fanjiang [1 ]
Han, En-Hou [1 ]
Wang, Jianqiu [1 ]
Zhang, Zhiming [1 ]
Me, Wei [1 ]
机构：
[1] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
来源：
ELECTROCHIMICA ACTA | 2011年 / 56卷 / 04期
关键词：
Scratch; Localized corrosion; SECM; Crack initiation; Alloy; 690; SCANNING ELECTROCHEMICAL MICROSCOPY; OXIDATION; CRACKING; WATER;
D O I：
10.1016/j.electacta.2010.08.028
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Localized corrosion of scratched Alloy 690TT was studied using scanning electrochemical microscopy (SECM) in 10 wt.% NaOH solution and atomic force microscopy (AFM) after short-time oxidation tests in high temperature high pressure water at 250 degrees C. The results show that the scratches detected by SECM displayed more extensive electrochemical activity. The scratch groove and the whole deformed region caused by scratching as anode corresponded to the peak of tip current. The oxides formed in 250 degrees C high purity pressurized water nucleated preferentially at the scratch groove and grew faster than non-scratched surface. The nano-grained scratch groove has more electrochemical reactivity than mechanical twins at scratch banks. The intense localized corrosion could contribute to crack initiation at the bottom of scratch groove. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1781 / 1785
页数：5
相关论文
共 50 条
  • [1] The role of hydrogen on lead-induced localized corrosion of Alloy 690TT
    Li, Weipeng
    Mi, Zhishan
    He, Yang
    Han, Yaolei
    Shi, Fangjie
    Peng, Qunjia
    Qiao, Lijie
    CORROSION SCIENCE, 2024, 240
  • [2] Stress corrosion cracking behavior and mechanism of scratched Alloy 690TT in lead-containing caustic solution
    Li, Z. H.
    You, L.
    Wang, L.
    Zhang, X. F.
    Su, Y.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2025, 245
  • [3] Size effect of scratches on the degradation behavior of alloy 690TT in high temperature caustic solution
    Wang, X. Y.
    Li, Z. H.
    Bai, Y. K.
    Cao, X. Y.
    Liu, T. G.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2021, 182
  • [4] Effect of Surface Scratch on Corrosion Behavior of Alloy 690TT Heat Exchanger Tubes
    Meng F.
    Wu B.
    Lv Y.
    Ming H.
    Bao Y.
    Wang J.
    Han E.-H.
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2021, 35 (11): : 827 - 834
  • [5] Effect of temperature on corrosion fatigue behavior of Inconel Alloy 690TT steam generator tube
    Li, Z. H.
    Lu, Y. H.
    You, L.
    Zhang, X. F.
    Wang, L.
    Tian, D. H.
    Zhang, W. D.
    Shoji, T.
    CORROSION SCIENCE, 2024, 227
  • [6] Effects of dissolved hydrogen on general corrosion behavior and oxide films of alloy 690TT in PWR primary water
    Jeon, Soon-Hyeok
    Lee, Eun-Hee
    Hur, Do Haeng
    JOURNAL OF NUCLEAR MATERIALS, 2017, 485 : 113 - 121
  • [7] Microstructural characteristics of Alloy 690TT subjected to fretting corrosion in high temperature water
    Xin, Long
    Yang, Beibei
    Li, Jie
    Lu, Yonghao
    Shoji, Tetsuo
    CORROSION SCIENCE, 2017, 123 : 116 - 128
  • [8] Mechanical polishing, surface roughness, near-surface deformation, and electrochemical corrosion of Alloy 690TT
    Arjmand, Farzin
    Zhang, Lefu
    SURFACE AND INTERFACE ANALYSIS, 2015, 47 (12) : 1120 - 1126
  • [9] Effects of scratching on corrosion and stress corrosion cracking of Alloy 690TT at 58 °C and 330 °C
    Meng, Fanjiang
    Wang, Jianqiu
    Han, En-Hou
    Ke, Wei
    CORROSION SCIENCE, 2009, 51 (11) : 2761 - 2769
  • [10] The single effect of microstructure, residual strain and geometric structure on the stress corrosion cracking behavior of scratched alloy 690TT
    Wu, Bin
    Ming, Hongliang
    Li, Rongbo
    Meng, Fanjiang
    Wang, Jianqiu
    Han, En-Hou
    CORROSION SCIENCE, 2024, 227
12345