Corrosion Resistance of Inconel 625 Overlay Welded Inside Pipes as a Function of Heat Treatment Temperature

被引：23
作者：
Ban, So-dam [1 ]
Shin, Young-Taek [2 ]
Lee, Sung Riong [3 ]
Lee, Hae-woo [1 ]
机构：
[1] Dong A Univ, Dept Mat Sci & Engn, Busan, South Korea
[2] Dong A Univ, Dept Naval Architecture & Offshore Engn, Busan, South Korea
[3] Kangwon Natl Univ, Departmnet Mat & Met Engn, Kangwon Do, South Korea
来源：
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2016年 / 11卷 / 09期
关键词：
Inconel; 625; Gas metal arc welding; overlay; potentiodynamic test; DL-EPR test; NI-BASE ALLOYS; BEHAVIOR; MICROSTRUCTURE; PRECIPITATION;
D O I：
10.20964/2016.09.22
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The effect of the heat treatment temperature on the corrosion resistance and precipitation of weld overlaid Inconel 625 has been investigated. Gas metal arc welding was performed using Inconel 625 as a filler metal with the ASTM A333Gr 6. The heat treatment was carried out on test specimens at 650 degrees C, 750 degrees C, 850 degrees C, and 950 degrees C for 24 hours. After heat treatment, the microstructure and elemental composition was investigated. At 650 degrees C, the specimen showed a dendritic pattern, and secondary phases was observed, whereas the fine gamma '''-phase observed at 750 degrees C At 850 degrees C the delta-phase was clearly observed, which was dissolved in the matrix at 950 degrees C and no longer visible. In addition, potentiodynamic polarization tests were performed to evaluate the pitting corrosion resistance. The results confirmed that there were no significant differences between the specimens. Double loop electrochemical potentiokinetic reactivationtests were undertaken to characterize the sensitization against intergranular corrosion. These results clearly showed that no sensitization occurred at any of the heat-treatment temperatures tested here.
引用
收藏
页码：7764 / 7774
页数：11
相关论文
共 25 条
  • [1] Laser cladding of Inconel 625 wire for corrosion protection
    Abioye, T. E.
    McCartney, D. G.
    Clare, A. T.
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 217 : 232 - 240
  • [2] [Anonymous], 127322008 ISO
  • [3] Melting and solidification study of Alloy 625
    Cieslak, M.J.
    Headley, T.J.
    Kollie, T.
    Romig Jr., A.D.
    [J]. Metallurgical transactions. A, Physical metallurgy and materials science, 1988, 19 A (09): : 2319 - 2331
  • [4] Cíhal V, 2001, ELECTROCHIM ACTA, V46, P3867
  • [5] FERRER L, 1991, P INT S METALLURGY A, P217
  • [6] Ganesan P., 1991, Superalloys, V718, P625
  • [7] Hassan S., 2011, THESIS, P19
  • [8] THE EFFECTS OF HEAT-TREATMENT ON THE CHROMIUM DEPLETION, PRECIPITATE EVOLUTION, AND CORROSION RESISTANCE OF INCONEL ALLOY-690
    KAI, JJ
    YU, GP
    TSAI, CH
    LIU, MN
    YAO, SC
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (10): : 2057 - 2067
  • [9] Lippold JC, 2015, WELDING METALLURGY AND WELDABILITY, P1
  • [10] Maguire M.C, 1994, SUPERALLOYS 718, 625, 706 AND VARIOUS DERIVATIVES, P881
123