A thermodynamic study of the D03-ordered intermetallic compound Fe3Al

被引：5
作者：
Huang, Yongzhang [3 ]
Yuan, Wenxia [2 ]
Qiao, Zhiyu [3 ]
Semenova, Olga [1 ]
Bester, Gabriel [4 ]
Ipser, Herbert [1 ]
机构：
[1] Univ Vienna, Dept Inorgan Chem Mat Chem, A-1090 Vienna, Austria
[2] Beijing Univ Sci & Technol, Dept Chem, Sch Appl Sci, Beijing 100083, Peoples R China
[3] Beijing Univ Sci & Technol, Sch Met & Ecol Engn, Beijing 100083, Peoples R China
[4] Natl Renewable Energy Lab, Golden, CO 80401 USA
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2008年 / 458卷 / 1-2期
基金：
奥地利科学基金会; 中国国家自然科学基金;
关键词：
metals and alloys; intermetallics; electromotive force; EMF; thermodynamic properties; thermodynamic modeling;
D O I：
10.1016/j.jallcom.2007.04.208
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Thermodynamic activities of aluminum in the iron-aluminum system were determined between about 720 and 850 K for the composition range between 23 and 33 at.% Al which includes the D0(3)-ordered nonstoichiometric intermetallic compound Fe3Al For this purpose an electromotive force method with a single-crystal CaF2 electrolyte was used, and the following cell arrangement was employed: (-)Pt vertical bar Ir vertical bar Al0.85Sn0.15, Na3AlF(6)vertical bar CaF2 vertical bar Al1 +/- xFe3 +/- x, Na3AlF6 vertical bar Ir vertical bar Pt(+). Activities of iron were obtained by means of a Gibbs-Duhem integration for the same composition range. The results of the activity measurements were interpreted in terms of a statistical-thermodynamic model for nonstoichiometric phases with the D0(3)-superstructure based on defect formation energies from the literature. It was found that non-stoichiometry in Fe3Al is caused by anti-structure atoms on two of the three possible sublattices. (c) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码：277 / 281
页数：5
相关论文
共 50 条
[31]   Magnetic properties of intermetallic compound Ti3Al with deuterium [J].
Patselov, A. ;
Milyaev, M. ;
Eshchenko, R. .
MAGNETISM AND MAGNETIC MATERIALS V, 2012, 190 :213-216
[32]   Neutron diffraction study on site occupation of substitutional elements at sub lattices in Fe3Al intermetallics [J].
Sun, ZQ ;
Yang, WY ;
Shen, LZ ;
Huang, YD ;
Zhang, BS ;
Yang, JL .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 258 (1-2) :69-74
[33]   Comparison of iron aluminide Fe3Al with armour steel in ballistic behaviour [J].
Hanus, Pavel ;
Pecanac, Milan ;
Trivkovic, Mirjana ;
Bojic, Savo ;
Balos, Sebastian .
DEFENCE TECHNOLOGY, 2024, 42 :183-190
[34]   Electrochemical Behavior of Fe3Al Modified with Ni in Hank's Solution [J].
Arrieta-Gonzalez, C. D. ;
Porcayo-Calderon, J. ;
Salinas-Bravo, V. M. ;
Gonzalez-Rodriguez, J. G. ;
Chacon-Nava, J. G. .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2011, 6 (09) :4016-4031
[35]   Tribological properties of a Fe3Al material in sulfuric acid corrosive environment [J].
Ma, Jiqiang ;
Hao, Junying ;
Bi, Qinling ;
Fu, LiCai ;
Yang, Jun ;
Liu, Weimin .
WEAR, 2010, 268 (1-2) :264-268
[36]   Preparation of nanocrystalline Al3Ti/Al13(Fe, Ni)4 intermetallic compound by means of melt spinning and subsequent annealing [J].
Tavoosi, Majid .
JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 688 :808-815
[37]   HIGH-TEMPERATURE PROPERTIES OF Fe3Al WITH ADDITION OF 2 AT.% OF Zr [J].
Kejzlar, Pavel ;
Svec, Martin .
METAL 2015: 24TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2015, :1488-1492
[38]   An assessment of the entire Al-Fe system including D03 ordering [J].
Sundman, Bo ;
Ohnuma, Ikuo ;
Dupin, Nathalie ;
Kattner, Ursula R. ;
Fries, Suzana G. .
ACTA MATERIALIA, 2009, 57 (10) :2896-2908
[39]   3-D morphology and growth mechanism of primary Al6Mn intermetallic compound in directionally solidified Al-3at.%Mn alloy [J].
Kang, Huijun ;
Li, Xinzhong ;
Su, Yanqing ;
Liu, Dongmei ;
Guo, Jingjie ;
Fu, Hengzhi .
INTERMETALLICS, 2012, 23 :32-38
[40]   Influence of Sintering Temperature on the Structure and Properties of Powder Iron Aluminide Fe3Al [J].
Tolochyn, O. I. ;
Tolochyna, O. V. ;
Bagliuk, H. A. ;
Yevych, Ya. I. ;
Podrezov, Yu. M. ;
Mamonova, A. A. .
POWDER METALLURGY AND METAL CERAMICS, 2020, 59 (3-4) :150-159
12345