Influence of Ga and Bi on electrochemical performance of Al-Zn-Sn sacrificial anodes

被引:36
作者
He Jun-guang [1 ,2 ]
Wen Jiu-ba [2 ]
Li Xu-dong [1 ]
Wang Guo-wei [2 ]
Xu Chun-hua [2 ]
机构
[1] Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China
[2] Henan Univ Sci & Technol, Sch Mat Sci & Engn, Luoyang 471003, Peoples R China
关键词
aluminium; sacrificial anode; electrochemical performance; electrochemical impedance spectroscopy; segregation; MG ALLOYS; ALUMINUM; ELECTROLYTES; CORROSION; BEHAVIOR; GALLIUM;
D O I
10.1016/S1003-6326(11)60900-X
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The influence of Ga and Bi on the microstructure and electrochemical performance of Al-7Zn-0.1Sn (mass fraction, %) sacrificial anodes was investigated by means of optical microscopy (OM), scanning electron microscopy/energy dispersive X-ray analysis (SEM/EDAX) and electrochemical measurements. It was found that the coarse dendrites structure transformed into the equiaxed grains as well as a small amount of dendrite grains after adding Ga and Bi into Al-Zn-Sn alloys. A high current efficiency of 97% and even corrosion morphology were obtained for Al-7Zn-0.1Sn-0.015Ga-0.1Bi alloy. The results indicate that the proper amount of Ga and Bi is effective on improving the microstructure and electrochemical performance of Al-Zn-Sn alloy.
引用
收藏
页码:1580 / 1586
页数:7
相关论文
共 19 条
[1]   THE ELECTROCHEMICAL-BEHAVIOR OF ALUMINUM ACTIVATED BY GALLIUM IN AQUEOUS-ELECTROLYTES [J].
BRESLIN, CB ;
CARROLL, WM .
CORROSION SCIENCE, 1992, 33 (11) :1735-1746
[2]   EIS STUDY OF HEAT-TREATED AL-ZN-MG ALLOYS IN THE PASSIVE AND TRANSPASSIVE POTENTIAL REGIONS [J].
CABOT, PL ;
GARRIDO, JA ;
PEREZ, E ;
MOREIRA, AH ;
SUMODJO, PTA ;
PROUD, W .
ELECTROCHIMICA ACTA, 1995, 40 (04) :447-454
[3]   Aluminium activation produced by gallium [J].
Flamini, D. O. ;
Saidman, S. B. ;
Bessone, J. B. .
CORROSION SCIENCE, 2006, 48 (06) :1413-1425
[4]  
*GB, 1999, GB178481999
[5]  
*GB, 2002, GB49482002
[6]   Solidification of chill-cast Al-Zn-Mg alloys to be used as sacrificial anodes [J].
Gonzalez, C ;
Alvarez, O ;
Genesca, J ;
Juarez-Islas, JA .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (12) :2991-2997
[7]  
GURRAPPA I, 1994, CORROS PREVENT CONTR, V41, P117
[8]   GALVANIC CORROSION CHARACTERISTICS OF ALUMINUM ALLOYED WITH GROUP 4 METALS [J].
KEIR, DS ;
PRYOR, MJ ;
SPERRY, PR .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1967, 114 (08) :777-&
[9]   THE EFFECT OF GALLIUM AND PHOSPHORUS ON THE CORROSION BEHAVIOR OF ALUMINUM IN SODIUM-CHLORIDE SOLUTION [J].
MANCE, A ;
CEROVIC, D ;
MIHAJLOVIC, A .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 1985, 15 (03) :415-420
[10]   Gel formation and the efficiency of anodic film growth on aluminium [J].
Morlidge, JR ;
Skeldon, P ;
Thompson, GE ;
Habazaki, H ;
Shimizu, K ;
Wood, GC .
ELECTROCHIMICA ACTA, 1999, 44 (14) :2423-2435