Preparation and fine thermal insulation performance of Gd2Zr2O7/ZrO2 composite fibers

被引：11

作者：

Chen, Jingwei ^{[1
,2
,3
]}

Wang, Xinqiang ^{[1
,2
]}

Xie, Yongshuai ^{[1
,2
]}

Shi, Shuying ^{[1
,2
]}

Zhang, Guanghui ^{[1
,2
]}

Zhu, Luyi ^{[1
,2
]}

机构：

[1] Shandong Univ, State Key Lab Crystal Mat, Jinan 250100, Peoples R China

[2] Shandong Univ, Inst Crystal Mat, Jinan 250100, Peoples R China

[3] Shandong Univ Technol, Sch Phys & Optoelect Engn, Zibo 255000, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2020年 / 46卷 / 02期

基金：

中国国家自然科学基金;

关键词：

Zirconate; Composite fibers; Electro-spinning; Thermal-physical properties; Thermal insulation; THERMOPHYSICAL PROPERTIES; MECHANICAL-PROPERTIES; CONDUCTIVITY; NANOCRYSTALS; A(2)B(2)O(7); SPECTROSCOPY; PYROCHLORE; YB2O3;

D O I：

10.1016/j.ceramint.2019.09.133

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Gd2Zr2O7/ZrO2 (GZC) composite fibers were prepared by electro-spinning method. The XRD, XPS and Raman results showed that there were three crystalline phases, tetragonal phase ZrO2, cubic phase ZrO2 and defect fluorite phase Gd2Zr2O7 in GZC composite fibers. GZC fibers remained an intact fiber texture up to 1400 degrees C according to SEM photographs. The thermal conductivity of GZC fibers was between 0.173 W/(m-K) at 400 degrees C and 0.309 W/(m-K) at 800 degrees C, which was lower than that of 7YSZ under the same experimental conditions. The fiber sheet with density about 3.5 g/cm(3) has thermal shrinkage less than 3% at 1400 degrees C. Hence, GZC fibers could be used as refractories for heat protection.

引用

页码：1615 / 1620

页数：6

共 50 条

[21] Gd2Zr2O7 and Nd2Zr2O7 pyrochlore prepared by aqueous chemical synthesis
Kong, Linggen
Karatchevtseva, Inna
Gregg, Daniel J.
Blackford, Mark G.
Holmes, Rohan
Triani, Gerry
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2013, 33 (15-16) : 3273 - 3285
[22] Interface failure behavior of yttria stabilized zirconia (YSZ), La2Zr2O7, Gd2Zr2O7, YSZ/La2Zr2O7 and YSZ/Gd2Zr2O7 thermal barrier coatings (TBCs) in thermal cyclic exposure
Karaoglanli, Abdullah Cahit
Doleker, Kadir Mert
Ozgurluk, Yasin
MATERIALS CHARACTERIZATION, 2020, 159
[23] Thermal shock performance and microstructure of advanced multilayer thermal barrier coatings with Gd2Zr2O7 topcoat
Sadri, Ehsan
Ashrafizadeh, Fakhreddin
Eslami, Abdoulmajid
Jazi, Hamidreza Salimi
Ehsaei, Hossein
SURFACE & COATINGS TECHNOLOGY, 2022, 448
[24] Effect of Ti substitution for Zr on the thermal expansion property of fluorite-type Gd2Zr2O7
Liu, Zhan-Guo
Ouyang, Jia-Hu
Zhou, Yu
Xia, Xiao-Liang
MATERIALS & DESIGN, 2009, 30 (09) : 3784 - 3788
[25] Temperature Dependence of the Thermal Conductivity of Gd2Zr2O7 Thin Films
Kang, Jun Gu
Kwak, J. H.
Yang, Ho-Soon
JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 2015, 66 (04) : 621 - 624
[26] Evolution of hot corrosion resistance of YSZ, Gd2Zr2O7, and Gd2Zr2O7 + YSZ composite thermal barrier coatings in Na2SO4 + V2O5 at 1050 °C
Habibi, M. H.
Wang, Li
Guo, S. M.
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2012, 32 (08) : 1635 - 1642
[27] Performance of YSZ and Gd2Zr2O7/YSZ double layer thermal barrier coatings in burner rig tests
Vassen, Robert
Bakan, Emine
Mack, Daniel
Schwartz-Lueckge, Sigrid
Sebold, Doris
Sohn, Yoo Jung
Zhou, Dapeng
Guillon, Olivier
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2020, 40 (02) : 480 - 490
[28] XANES Spectroscopic Studies of the Phase Transition in Gd2Zr2O7
Lee, Yu-Hsuen
Chen, Jin-Ming
Lee, Jyh-Fu
Kao, Huey-Chuen I.
JOURNAL OF THE CHINESE CHEMICAL SOCIETY, 2009, 56 (03) : 543 - 548
[29] Synthesis and photoluminescence properties of Eu3+-doped Gd2Zr2O7
Hu, Kai-Jun
Liu, Zhan-Guo
Wang, Jun-Yao
Wang, Tao
Ouyang, Jia-Hu
MATERIALS LETTERS, 2012, 89 : 276 - 278
[30] Pressure induced structural transformation in Gd2Ti2O7 and Gd2Zr2O7
Xiao, H. Y.
Weber, W. J.
JOURNAL OF PHYSICS-CONDENSED MATTER, 2011, 23 (03)

← 1 2 3 4 5 →