Influence of several fibre-reinforced composite restoration techniques on cusp movement and fracture strength of molar teeth

被引:29
作者
Akman, S. [2 ]
Akman, M. [1 ]
Eskitascioglu, G. [3 ]
Belli, S. [1 ]
机构
[1] Selcuk Univ, Fac Dent, Dept Endodont, TR-42079 Konya, Turkey
[2] Selcuk Univ, Fac Dent, Dept Prosthodont, TR-42079 Konya, Turkey
[3] Yuzuncu Yil Univ, Fac Dent, Dept Prosthodont, Van, Turkey
关键词
cuspal deflection; cuspal movement; fibre-reinforced composites; endodontically treated teeth; loading; topographical mesurement; ENDODONTICALLY-TREATED TEETH; POLYMERIZATION SHRINKAGE; IN-VITRO; FLOWABLE RESIN; HUMAN DENTIN; MECHANICAL-PROPERTIES; DEFLECTION; DEFORMATION; RESISTANCE; STRESS;
D O I
10.1111/j.1365-2591.2010.01843.x
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
P>Aim To compare mean cusp movement in molar teeth with endodontic access and mesial-occlusal-distal (MOD) cavities before and after restoration with several fibre-reinforced composite restoration techniques under loading and to evaluate the effect of restoration technique on fracture strength. Methodology Reference points were marked at the mesial cusp ridges of extracted human mandibular molar teeth. Digital images were taken under loading (300 N) using a stereomicroscope (Leica MZ16A; Wetzlar, Germany). Three-dimensional (3D) distances between the reference points were recorded (Leica, Stereo-Explorer, 2.1) as controls. Standard MOD cavities were prepared and restored as follows (n = 10), group 1: composite restoration (Clearfil AP-X; Kuraray, Tokyo, Japan); group 2: cavity lined with polyethylene fibre (Ribbond, Ribbond Inc., Seattle, WA, USA) in combination with flowable resin (Protect-Liner F; Kuraray, Tokyo, Japan) before composite restoration; group 3: polyethylene fibre inserted on occlusal surface of the tooth from buccal to lingual after finishing the composite restoration; group 4: missing walls were restored with composite resin and inner surfaces of the axial walls were then reinforced with polyethylene fibre placed circumferentially before the composite restoration. The restored teeth were re-loaded, digital images were re-taken and the 3D distance between the reference points was recorded in mu m. Comparisons of the restoration techniques, the effectiveness of restoration for each group were analysed statistically (Kruskall-Wallis, paired-samples t-test). The teeth were then loaded until failure (5 mm min-1), the data were recorded (N) and analysed statistically (Kruskall-Wallis test). Results A significant difference occurred amongst the groups in terms of cusp movement (P = 0.018). All the groups revealed a decrease in inter-cuspal width when compared to their initial records. The mean values of these decreases were as follows: group 1 17.6 (P = 0.003), group 2 6.7 (not sig), group 3 6.6 (not sig) and group 4 0.85 (not sig) mu m. No significant difference was found amongst the fracture strength values (P = 0.22). In group 1, 90% of the fractures were non-restorable, whereas in group 3 100% of the fractures were restorable. Conclusions Regardless of restoration technique, fibre reinforcement of composite restorations decreased cusp movement in molar teeth with MOD and endodontic access cavities but did not affect fracture strength.
引用
收藏
页码:407 / 415
页数:9
相关论文
共 48 条
[1]  
Alomari QD, 2001, OPER DENT, V26, P406
[2]   Assessment of in vitro methods used to promote adhesive interface degradation: A critical review [J].
Amaral, Flavia L. B. ;
Colucci, Vivian ;
Palma-Dibb, Regina G. ;
Corona, Silmara A. M. .
JOURNAL OF ESTHETIC AND RESTORATIVE DENTISTRY, 2007, 19 (06) :340-353
[3]  
BAUSCH JR, 1982, J PROSTHET DENT, V48, P59, DOI 10.1016/0022-3913(82)90048-8
[4]   Reinforcement effect of polyethylene fibre in root-filled teeth: comparison of two restoration techniques [J].
Belli, S ;
Erdemir, A ;
Yildirim, C .
INTERNATIONAL ENDODONTIC JOURNAL, 2006, 39 (02) :136-142
[5]   Effect of hybrid layer on stress distribution in a premolar tooth restored with composite or ceramic inlay: An FEM study [J].
Belli, S ;
Eskitascioglu, G ;
Eraslan, O ;
Ssenawongse, P ;
Tagami, J .
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS, 2005, 74B (02) :665-668
[6]   The effect of fibre insertion on fracture resistance of root filled molar teeth with MOD preparations restored with composite [J].
Belli, S ;
Erdemir, A ;
Ozcopur, M ;
Eskitascioglu, G .
INTERNATIONAL ENDODONTIC JOURNAL, 2005, 38 (02) :73-80
[7]  
Belli S, 2008, COMPENDIUM SCI CLIN, P39
[8]  
Belli S, 2007, J ADHES DENT, V9, P175
[9]  
Belli S, 2006, J ADHES DENT, V8, P247
[10]   Cuspal deflection and microleakage in premolar teeth restored with resin-based composites with and without an intermediary flowable layer [J].
Cara, R. R. ;
Fleming, G. J. P. ;
Palin, W. M. ;
Walmsley, A. D. ;
Burke, F. J. T. .
JOURNAL OF DENTISTRY, 2007, 35 (06) :482-489