Surface structure of large synthetic diamonds by high temperature and high pressure

With NiMnCo and FeCoNi alloys as solvent metals, large single-crystal diamonds of about 3 mm across are grown by temperature gradient method (TGM) under high temperature and high pressure (HPHT). Although both {100} and {111} surfaces are developed by a layer growth mechanism, some different characteristic patterns are seen clearly on the different surfaces, no matter whether NiMnCo or FeCoNi alloys are taken as the solvent metals. For {100} surface, it seems to have been melted or etched greatly, no dendritic patterns to be found, and only a large number of growth hillocks are dispersed net-likely; while for {111} surface, it often seems to be more smooth-faced, no etched or melted traces are present even when a lot of depressed trigonal growth layers. This distinct difference between {111} and {100} surfaces is considered to be related to the difference of surface-atom distribution of different surfaces, and {111} surfaces should be more difficult to be etched and more steady than {100} surfaces.