On the tension-tension fatigue behaviour of a carbon reinforced thermoplastic part II: Evaluation of a dumbbell-shaped specimen

被引：51

作者：

De Baere, I. ^{[1
]}

Van Paepegem, W. ^{[1
]}

Hochard, C. ^{[2
]}

Degrieck, J. ^{[1
]}

机构：

[1] Univ Ghent, Fac Engn, Dept Mat Sci & Engn, B-9052 Zwijnaarde, Belgium

[2] Univ Aix Marseille, CNRS, Lab Mecan & Acoust, F-13402 Marseille 20, France

来源：

POLYMER TESTING | 2011年 / 30卷 / 06期

关键词：

Fatigue; Dumbbell; Carbon fibre; Thermoplastic; STRENGTH UNIDIRECTIONAL COMPOSITES; STRESS-STRAIN ANALYSIS; LOAD-TRANSFER ZONE; UNIAXIAL TENSION; COMPRESSIVE STRENGTH; FRAGMENTATION TEST; FLAT SPECIMENS; FIBER; DESIGN; DAMAGE;

D O I：

10.1016/j.polymertesting.2011.05.005

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

For performing uni-axial fatigue tests on composite materials, ASTM D3479/D3479M Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials is often considered. This standard prescribes a rectangular shaped specimen with end tabs. However, in part I of this study it became clear that for some materials, such as the carbon PPS under study, the proposed geometry is not ideal for fatigue tests. In this manuscript, a dumbbell (dogbone) shape is assessed to see whether it performs better under fatigue loading conditions, primarily meaning that failure does not occur in the tabbed section. The shape is first optimised using finite element modelling, after which fatigue experiments are performed. It may be concluded, for the material under study, that the dumbbell shape is preferable to rectangular since failure never occurred under or near the tabbed section, and fatigue life is highly underestimated when using the rectangular specimen. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：663 / 672

页数：10

共 19 条

[1] Design selection methodology for composite structures [J].

Aceves, C. Monroy ;

Skordos, A. A. ;

Sutcliffe, M. P. F. .

MATERIALS & DESIGN, 2008, 29 (02) :418-426

[2]

ANDREW L, 1998, GYEKENYESI ISOTHERMA

[3] AN IMPROVED ENGINEERING TEST METHOD FOR MEASUREMENT OF THE COMPRESSIVE STRENGTH OF UNIDIRECTIONAL CARBON-FIBER COMPOSITES [J].

CURTIS, PT ;

GATES, J ;

MOLYNEUX, CG .

COMPOSITES, 1991, 22 (05) :363-368

[4]

DAGGUMATI S, COMPOSITE S IN PRESS

[5] Comparison of different identification techniques for measurement of quasi-zero Poisson's ratio of fabric-reinforced laminates [J].

De Baere, I. ;

Van Paepegem, W. ;

Degrieck, J. ;

Sol, H. ;

Van Hemelrijck, D. ;

Petreli, A. .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2007, 38 (09) :2047-2054

[6] On the tension-tension fatigue behaviour of a carbon reinforced thermoplastic part I: Limitations of the ASTM D3039/D3479 standard [J].

De Baere, I. ;

Van Paepegem, W. ;

Quaresimin, M. ;

Degrieck, J. .

POLYMER TESTING, 2011, 30 (06) :625-632

[7] On the Design of End Tabs for Quasi-Static and Fatigue Testing of Fibre-Reinforced Composites [J].

De Baere, I. ;

Van Paepegem, W. ;

Degrieck, J. .

POLYMER COMPOSITES, 2009, 30 (04) :381-390

[8] Analysis of fatigue and damage in glass-fibre-reinforced polypropylene composite materials [J].

Ferreira, JAM ;

Costa, JDM ;

Reis, PNB ;

Richardson, MOW .

COMPOSITES SCIENCE AND TECHNOLOGY, 1999, 59 (10) :1461-1467

[9] Optimum design of laminated composite structures [J].

Hochard, C .

COMPOSITE STRUCTURES, 2004, 63 (02) :159-165

[10] An automated testing machine for monitoring the evolution of fiber breaks [J].

Holmes, G. A. ;

Wesson, Sheldon ;

McDonough, W. G. ;

Kim, J. H. ;

Netravali, A. ;

Walker, J. N. ;

Johnson, R. A. .

JOURNAL OF MATERIALS SCIENCE, 2009, 44 (08) :2007-2015

← 1 2 →