Improvement of anti-corrosive properties of epoxy-coated AA 2024-T3 with TiO2 nanocontainers loaded with 8-hydroxyquinoline

被引：115
作者：
Balaskas, A. C. [1 ]
Kartsonakis, I. A. [1 ,2 ]
Tziveleka, L-A [1 ]
Kordas, G. [1 ]
机构：
[1] NCSR Demokritos, IMS, Sol Gel Lab, Aghia Paraskevi 15310, Greece
[2] NTUA, Sch Chem Engn, Zografos 15780, Greece
来源：
PROGRESS IN ORGANIC COATINGS | 2012年 / 74卷 / 03期
关键词：
AA2024-T3; Nanocontainers; Corrosion; Self-healing; EIS; SOL-GEL COATINGS; CORROSION PROTECTION; HEXAVALENT CHROMIUM; SILANE FILMS; ALUMINUM; PERFORMANCE; INHIBITION; INTERLAYER; CONVERSION; CANCER;
D O I：
10.1016/j.porgcoat.2012.01.005
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Epoxy coatings containing TiO2 nanocontainers were applied on aluminium alloy (AA) 2024-T3 for corrosion protection. The nanocontainers were loaded with the corrosion inhibitor 8-hydroxyquinoline (8-HQ). Epoxy coatings were deposited via the dip-coating process. The morphology of the coatings was examined by scanning electron microscopy (SEM). The composition of the films was determined by energy dispersive X-ray analysis (EDX). Electrochemical impedance spectroscopy (EIS) was employed for the characterization of the corrosion resistance of these coatings. The total impedance values were measured as a function of time exposure in corrosive environment. We observed a continuous increase of the total impedance value with the time of exposure suggesting a possible self-healing effect due to the release of the inhibitors from the nanocontainers. Furthermore, addition of loaded nanocontainers into the coatings leads to the enhancement of the barrier properties of the coatings. Conclusively, we observed an improvement of the performance of the coatings due to the loaded nanocontainers. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码：418 / 426
页数：9
相关论文
共 35 条
[1]   Improving the corrosion protection properties of organically modified silicate-epoxy coatings by incorporation of organic and inorganic inhibitors [J].
Balaskas, A. C. ;
Kartsonakis, I. A. ;
Snihirova, D. ;
Montemor, M. F. ;
Kordas, G. .
PROGRESS IN ORGANIC COATINGS, 2011, 72 (04) :653-662
[2]   Mesoporous Silica Nanoparticles for Active Corrosion Protection [J].
Borisova, Dimitriya ;
Moehwald, Helmuth ;
Shchukin, Dmitry G. .
ACS NANO, 2011, 5 (03) :1939-1946
[3]   A COMPILATION OF CORROSION POTENTIALS REPORTED FOR INTERMETALLIC PHASES IN ALUMINUM-ALLOYS [J].
BUCHHEIT, RG .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (11) :3994-3996
[4]   Local dissolution phenomena associated with S phase (Al2CuMg) particles in aluminum alloy 2024-T3 [J].
Buchheit, RG ;
Grant, RP ;
Hlava, PF ;
Mckenzie, B ;
Zender, GL .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (08) :2621-2628
[5]   Preparation, characterization and thermal properties of nanocapsules containing phase change material n-dodecanol by miniemulsion polymerization with polymerizable emulsifier [J].
Chen, Zhong-Hua ;
Yu, Fei ;
Zeng, Xing-Rong ;
Zhang, Zheng-Guo .
APPLIED ENERGY, 2012, 91 (01) :7-12
[6]   Inhibitory action of 8-hydroxyquinoline on the copper corrosion process [J].
Cicileo, GP ;
Rosales, BM ;
Varela, FE ;
Vilche, JR .
CORROSION SCIENCE, 1998, 40 (11) :1915-1926
[7]   Inhibitor-doped sol-gel coatings for corrosion protection of magnesium alloy AZ31 [J].
Galio, A. F. ;
Lamaka, S. V. ;
Zheludkevich, M. L. ;
Dick, L. F. P. ;
Mueller, I. L. ;
Ferreira, M. G. S. .
SURFACE & COATINGS TECHNOLOGY, 2010, 204 (9-10) :1479-1486
[8]   An investigation of the corrosion inhibition of pure aluminum in neutral and acidic chloride solutions [J].
Garrigues, L ;
Pebere, N ;
Dabosi, F .
ELECTROCHIMICA ACTA, 1996, 41 (7-8) :1209-1215
[9]   Technical note:: Concerning the conversion of the constant phase element parameter Y0 into a capacitance [J].
Hsu, CH ;
Mansfeld, F .
CORROSION, 2001, 57 (09) :747-748
[10]   The effect of precipitation-hardening conditions on wear behaviours at 2024 alurninium wrought alloy [J].
Kacar, H ;
Atik, E ;
Meric, C .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 142 (03) :762-766
1234