Lithium insertion properties of mesoporous nanocrystalline TiO2 and TiO2-V2O5 microspheres prepared by non-hydrolytic sol-gel

Mesoporous nanocrystalline TiO2 and TiO2-V2O5 microspheres were prepared by non-hydrolytic sol-gel from TiCl4, VOCl3, and (Pr2O)-Pr-i at 110 A degrees C without any solvent or additives. The samples were characterized by elemental analysis, X-ray diffraction, Raman spectroscopy, scanning electron microscopy, nitrogen physisorption, and impedance measurements. At low vanadium loadings, only TiO2 anatase was detected, and V2O5 scherbinaite was also detected at high vanadium loadings. The texture of the samples depended on the V loading, but all the samples appeared built of primary nanoparticles (ae10-20 nm in size) that aggregate to form mesoporous micron-sized spheres. The lithium insertion properties of these materials were evaluated by galvanostatic measurements taken using coin-type cells, in view of their application as electrode for rechargeable Li-ion batteries. The mesoporous TiO2 microspheres showed good performances, with a specific reversible capacity of 145 and 128 mAh g(-1) at C/2 and C, respectively (C = 335.6 mA g(-1)), good coulombic efficiency, and a moderate capacity fade (6 %) from the 2nd to the 20th cycle at C/20. Although the addition of V effectively increased the electronic conductivity of the powders, the specific reversible capacity and cycling performances of the TiO2-V2O5 samples were only minimally improved for a 5 at% V loading and were lower at higher V loading. [GRAPHICS]