Direct crystallisation of a hydroxy sodalite membrane without seeding using a conventional oven

被引：18
作者：
van Niekerk, Anelta
Zah, Jaco
Breytenbach, Jaco C.
Krieg, Henning M.
机构：
[1] NW Univ, Sch Pharm, ZA-2531 Potchefstroom, South Africa
[2] NW Univ, Sch Chem, ZA-2531 Potchefstroom, South Africa
来源：
JOURNAL OF MEMBRANE SCIENCE | 2007年 / 300卷 / 1-2期
关键词：
hydroxy socialite membrane; synthesis; conventional oven; single gas; permeance;
D O I：
10.1016/j.memsci.2007.05.021
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A double layered hydroxy sodalite membrane was synthesised directly onto a tubular alpha-alumina support without seeding using a conventional hot-air oven. The effect of different synthesis parameters including the water content, ageing period, synthesis time and temperature, on the purity and continuity of the membrane was investigated. The water content was an important factor in controlling the presence of contaminating zeolite phases in the membrane. The optimised membrane which was contaminant free was characterised by XRD, SEM and single gas permeation using He, N-2 and SF6. The permeance of the three gases through the membrane ranged from 0.8 to 8 x 10(-8) mol m(-2) s(-1) Pa-1. The selectivity (alpha = 2.5-2.7) compared well to the Knudsen diffusion ratio for He/N-2. (C) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码：156 / 164
页数：9
相关论文
共 21 条
[1]  
BAERLOCHER C, 2001, ALTAS ZEOLITE FRAMEW
[2]   Lower temperatures for the preparation of thinner zeolite A coatings [J].
Çetin, T ;
Tatlier, M ;
Erdem-Senatalar, A ;
Demirler, U ;
Ürgen, M .
MICROPOROUS AND MESOPOROUS MATERIALS, 2001, 47 (01) :1-14
[3]   The influence of gel properties on the kinetics of crystallization and particulate properties of MFI-type zeolites. I. The influence of time and temperature of gel ageing on the particulate properties of silicalite-1 microcrystals [J].
Cizmek, A ;
Subotica, B ;
Kralj, D ;
Babic-Ivancic, V ;
Tonejc, A .
MICROPOROUS MATERIALS, 1997, 12 (4-6) :267-280
[4]   ZEOLITE SYNTHESIS IN UNSTIRRED BATCH REACTORS .3. EFFECT OF NONUNIFORM PRE-MIXING ON THE CRYSTALLIZATION OF ZEOLITE-A AND ZEOLITE-X [J].
COKER, EN ;
DIXON, AG ;
THOMPSON, RW ;
SACCO, A .
MICROPOROUS MATERIALS, 1995, 3 (06) :637-646
[5]  
JANSEN JC, 2005, Patent No. 524254
[6]   Synthesis of sodalite/αAl2O3 composite membranes by microwave heating [J].
Julbe, A ;
Motuzas, J ;
Cazevielle, F ;
Volle, G ;
Guizard, C .
SEPARATION AND PURIFICATION TECHNOLOGY, 2003, 32 (1-3) :139-149
[7]   Dehydration of water/1-1-dimethylhydrazine mixtures by zeolite membranes [J].
Kazemimoghadam, M ;
Pak, A ;
Mohammadi, T .
MICROPOROUS AND MESOPOROUS MATERIALS, 2004, 70 (1-3) :127-134
[8]   Physical chemistry of aluminosilicate gels .1. Influence of batch concentration on chemical composition of the gels [J].
Krznaric, I ;
Antonic, T ;
Subotic, B .
ZEOLITES, 1997, 19 (01) :29-40
[9]   Physical chemistry of aluminosilicate gels.: Part 2 -: Influence of the batch molar ratio SiO2/Al2O3 on chemical composition of the gels [J].
Krznaric, I ;
Antonic, T ;
Subotic, B .
MICROPOROUS AND MESOPOROUS MATERIALS, 1998, 20 (1-3) :161-175
[10]   Vacuum seeding and secondary growth route to sodalite membrane [J].
Lee, SR ;
Son, YH ;
Julbe, A ;
Choy, JH .
THIN SOLID FILMS, 2006, 495 (1-2) :92-96
123