Temperature dependence of tensile behavior of Ni-based superalloy M951

被引：79

作者：

Lian, Z. W. ^{[1
]}

Yu, J. J. ^{[1
]}

Sun, X. F. ^{[1
]}

Guan, H. R. ^{[1
]}

Hu, Z. Q. ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 489卷 / 1-2期

关键词：

M951; alloy; tensile strength; ductility; dislocation;

D O I：

10.1016/j.msea.2008.02.013

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Tensile properties of M951 alloy are shown to be significantly dependent on temperatures in this study. Like in other superalloys, the yield and tensile strengths decreased slightly between room temperature and 600 degrees C, then both strengths showed peak values at intermediate temperatures, and both decreased sharply above 850 degrees C. The elongation fluctuated with temperature with its minimum at 800 degrees C. The TEM observations showed that at low temperature the dominant deformation mechanism was gamma' shearing by dislocation pairs and slip bands. At high temperature, the deformation was dominated by gamma' by-pass. At intermediate temperature it showed a transition from gamma' shearing to by-passing. (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：227 / 233

页数：7

共 28 条

[1] Tensile strengthening in the nickel-base superalloy IN738LC [J].

Balikci, E ;

Mirshams, RA ;

Raman, A .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2000, 9 (03) :324-329

[2]

BETTGE D, 1995, Z METALLKD, V86, P197

[3] IMPROVEMENT OF CREEP STRENGTH IN A NICKEL-BASE SINGLE-CRYSTAL SUPER-ALLOY BY HEAT-TREATMENT [J].

CARON, P ;

KHAN, T .

MATERIALS SCIENCE AND ENGINEERING, 1983, 61 (02) :173-184

[4]

Caron P., 1988, Superalloys 1988, P215

[5] Evidence of variation in slip mode in a polycrystalline nickel-base superalloy with change in temperature from neutron diffraction strain measurements [J].

Daymond, M. R. ;

Preuss, M. ;

Clausen, B. .

ACTA MATERIALIA, 2007, 55 (09) :3089-3102

[6]

DOLLAR M, 1988, SUPERALLOYS 1988, P275

[7] DISLOCATION-STRUCTURES IN GAMMA-GAMMA' INTERFACES OF THE SINGLE-CRYSTAL SUPERALLOY SRR-99 AFTER ANNEALING AND HIGH-TEMPERATURE CREEP [J].

FELLERKNIEPMEIER, M ;

LINK, T .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 113 :191-195

[8]

Fiore N.F., 1975, REV HIGH TEMP MAT, V2, P373

[9]

FLINN PA, 1960, T AM I MIN MET ENG, V218, P145

[10] Low ductility at intermediate temperature of Ni-base superalloy M963 [J].

He, LZ ;

Zheng, Q ;

Sun, XF ;

Hou, GC ;

Guan, HR ;

Hu, ZQ .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 380 (1-2) :340-348

← 1 2 3 →