Effect of Holes on Dynamic Crack Propagation under Impact Loading

被引:5
作者
Wang, Fei [1 ,2 ]
Wang, Meng [2 ]
机构
[1] Sichuan Univ, Key Lab Sichuan Prov, Failure Mech & Engn Disaster Prevent & Mitigat, Chengdu 610065, Peoples R China
[2] Sichuan Univ, Coll Architecture & Environm, Minist Educ, Key Lab Deep Underground Sci & Engn, Chengdu 610065, Peoples R China
来源
APPLIED SCIENCES-BASEL | 2020年 / 10卷 / 03期
基金
中国国家自然科学基金; 中国博士后科学基金;
关键词
impact loading; crack propagation; crack arrest; PMMA; numerical simulation; INITIATION; SPECIMENS; BEHAVIOR; GROWTH; ROCK;
D O I
10.3390/app10031122
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
In civil, geotechnical, and mining engineering, the investigation of the holes' effect on dynamic crack propagation is essential because it can be used to predict possible fracture and protect cracked structures being further damaged. In this paper, a specimen made from polymethyl methacrylate (PMMA) with a pre-crack and two holes was proposed, and the Split-Hopkinson pressure bar was employed to investigate the effect of holes on dynamic crack propagation under impact loading. Notably, the locations of the holes were well designed with different two-hole spacing (12 mm, 16 mm, and 20 mm) and crack-hole distance (15 mm, 30 mm, and 45 mm). Crack propagation gauges were applied to monitor the fracturing time and crack extending velocity. The interaction characteristic between the crack and two holes was studied numerically using the AUTODYN code. In the numerical models, the failure criteria of maximum tensile stress and softening damage were employed for brittle material. The crack path, the propagating velocity, the particle velocity vector, and the stress state between the holes were analyzed. The calculation results indicate that compressive stresses between the two holes induced by the deformation of the holes play a crucial role in confining the vertical crack propagation. Both experimental and numerical results demonstrate that the holes have a suppressing action on the moving crack; as the two-hole spacing decreases, the suppressing action intensifies.
引用
收藏
页数:18
相关论文
共 27 条
[1]   Mixed mode fatigue crack initiation and growth in a CT specimen repaired by stop hole technique [J].
Ayatollahi, Majid R. ;
Razavi, Nima ;
Yahya, Mohd Yazid .
ENGINEERING FRACTURE MECHANICS, 2015, 145 :115-127
[2]   A stop-hole method for marine and offshore structures [J].
Chen, Nian-Zhong .
INTERNATIONAL JOURNAL OF FATIGUE, 2016, 88 :49-57
[3]   NATURAL JOINTS IN ROCK - MECHANICAL, HYDRAULIC AND SEISMIC BEHAVIOR AND PROPERTIES UNDER NORMAL STRESS [J].
COOK, NGW .
INTERNATIONAL JOURNAL OF ROCK MECHANICS AND MINING SCIENCES & GEOMECHANICS ABSTRACTS, 1992, 29 (03) :198-223
[4]  
Eringen A., 1978, J APPL MECH, V45, DOI [10.1115/1.3424252, DOI 10.1115/1.3424252]
[5]   Theoretical and numerical investigation on in-plane impact performance of chiral honeycomb core structure [J].
Gao, Dianwei ;
Zhang, Chunwei .
JOURNAL OF STRUCTURAL INTEGRITY AND MAINTENANCE, 2018, 3 (02) :95-105
[6]   Local strain energy to assess the static failure of U-notches in plates under mixed mode loading [J].
Gomez, F. J. ;
Elices, M. ;
Berto, F. ;
Lazzarin, P. .
INTERNATIONAL JOURNAL OF FRACTURE, 2007, 145 (01) :29-45
[7]   Investigation of Dynamic Crack Coalescence Using a Gypsum-Like 3D Printing Material [J].
Jiang, Chao ;
Zhao, Gao-Feng ;
Zhu, Jianbo ;
Zhao, Yi-Xin ;
Shen, Luming .
ROCK MECHANICS AND ROCK ENGINEERING, 2016, 49 (10) :3983-3998
[8]   DYNAMIC INTERACTION OF A PROPAGATING CRACK WITH A HOLE BOUNDARY [J].
MILIOS, J ;
SPATHIS, G .
ACTA MECHANICA, 1988, 72 (3-4) :283-295
[9]   Interaction of an interfacial crack with linear small defects under out-of-plane shear loading [J].
Mishuris, G. ;
Movchan, A. ;
Movchan, N. ;
Piccolroaz, A. .
COMPUTATIONAL MATERIALS SCIENCE, 2012, 52 (01) :226-230
[10]   A crack-growth arresting technique in aluminum alloy [J].
Murdani, Anggit ;
Makabe, Chobin ;
Saimoto, Akihide ;
Kondou, Ryouji .
ENGINEERING FAILURE ANALYSIS, 2008, 15 (04) :302-310