Effect of the pH value of the hydrogenation solution upon the phase transformation of nickel into nickel hydride

被引:5
|
作者
Monev, M [1 ]
机构
[1] Bulgarian Acad Sci, Inst Phys Chem, BU-1113 Sofia, Bulgaria
关键词
nickel coatings; hydride formation; X-ray diffraction;
D O I
10.1016/S0013-4686(01)00438-8
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
The effect of pH value of the hydrogenation solution, containing H2SeO3 as a hydrogenation-enhancing additive upon the phase transformation of nickel into P-nickel hydride in electrodeposited bright nickel coatings during cathodic charging was studied using X-ray diffraction. The nickel hydride formation terminates at pH value over 2,1, At this pH value in the bulk of hydrogenation solution, the pH Value within the layer in the vicinity of the nickel electrode shift during the cathodic process to the alkaline region as a result of hydrogen evolution. An indication of the alkalization is the shift of the nickel electrode potential towards more negative values (- 1.3 V NHE) within the range of pH values where phase transformation terminates. The hydrogenation enhancing effect of H2SeO3 appears to occur when the deposition of selenium on nickel surface begins. Strong hydrogenation of samples with co-deposited selenium proceeds during cathodic polarization in an acidic medium without an enhancing additive. (C) 2001 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:2373 / 2378
页数:6
相关论文
共 50 条
  • [1] Peculiarities of nickel oxide structure transformation upon CO hydrogenation
    Morozova, OS
    Kryukova, GN
    Shashkin, DP
    Plyasova, LM
    Krylov, OV
    JOURNAL OF CATALYSIS, 1996, 158 (01) : 13 - 22
  • [2] Effect of Different pH Value Solution on Tribological Properties of Nickel-Based Coatings
    Qiao Lixia
    LASER & OPTOELECTRONICS PROGRESS, 2022, 59 (11)
  • [3] X-RAY-DIFFRACTION STUDY OF ANISOTROPY BY FORMATION AND DECOMPOSITION OF NICKEL HYDRIDE .1. ORIENTATION DEPENDENCE OF THE EXTENT OF PHASE-TRANSFORMATION OF NICKEL INTO NICKEL HYDRIDE
    TOMOV, I
    MONEV, M
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 1992, 22 (03) : 262 - 267
  • [4] Corrosion behavior of hydrogenated nickel and nickel hydride in sulfuric acid solution
    Markorosyan, GN
    Pchelnikov, AP
    Losev, VV
    PROTECTION OF METALS, 1997, 33 (05): : 454 - 456
  • [6] EFFECT OF REAL STRUCTURE OF NICKEL ON KINETICS OF NICKEL HYDRIDE DECOMPOSITION
    PIELASZEK, J
    LUNARSKA, E
    BULLETIN DE L ACADEMIE POLONAISE DES SCIENCES-SERIE DES SCIENCES CHIMIQUES, 1978, 26 (01): : 87 - 90
  • [7] Effect of initial solution apparent pH on nano-sized nickel catalysts in p-nitrophenol hydrogenation
    Chen, Rizhi
    Wang, Qinqin
    Du, Yan
    Xing, Weihong
    Xu, Nanping
    CHEMICAL ENGINEERING JOURNAL, 2009, 145 (03) : 371 - 376
  • [8] Effect of pH value on the electroless nickel plating on surface of diamond
    Yao, Huai
    Zhu, Yao-Min
    Zhu, Guang-Lin
    Rengong Jingti Xuebao/Journal of Synthetic Crystals, 2012, 41 (06): : 1629 - 1633
  • [9] EXPERIMENTS ON KONDO EFFECT IN NICKEL HYDRIDE
    BAUER, HJ
    KOHLER, KA
    DIETRICH, I
    KADEREIT, HG
    PHYSICS LETTERS A, 1970, A 31 (02) : 57 - &
  • [10] Hydrogenation catalysts from used nickel metal hydride batteries
    Foreman, Mark R. St J.
    Ekberg, Christian
    Jensen, Arvid Oedegaard
    GREEN CHEMISTRY, 2008, 10 (08) : 825 - 826