Transport model of chloride ions in concrete under loads and drying-wetting cycles

被引：98
|
作者：
Wu, Jin [1 ]
Li, Hongming [1 ]
Wang, Zhe [1 ]
Liu, Jingjing [1 ]
机构：
[1] Nanjing Univ Aeronaut & Astronaut, Dept Civil Engn, Nanjing 210016, Jiangsu, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2016年 / 112卷
基金：
中国国家自然科学基金;
关键词：
Concrete structures; Chloride ion; Drying-wetting cycles; Load; Diffusion coefficient; SERVICE-LIFE; PENETRATION; PREDICTION; DIFFUSION;
D O I：
10.1016/j.conbuildmat.2016.02.167
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Alternation of drying and wetting led to the worst corrosion of the engineering structures in marine environments. In this paper, the transport of chloride ions in concrete under loads and drying-wetting cycles was investigated. The influences of drying-wetting cycles, stress ratios and exposed ages of concrete on chloride ions transport in concrete were studied. The relationships between the coefficient of chloride ion diffusion and stress ratios of concrete under the loads and drying-wetting cycles were obtained. The relationship between the chloride ion concentration of concrete surface and exposed ages of concrete was studied. And the simplified transport model of chloride ions in concrete under loads and drying wetting cycles was established, of which the validity was verified through the good agreement with the experimental data. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：733 / 738
页数：6
相关论文
共 50 条
  • [41] Modeling of Concrete Deterioration under External Sulfate Attack and Drying-Wetting Cycles: A Review
    Qin, Shanshan
    Chen, Chuyu
    Zhang, Ming
    MATERIALS, 2024, 17 (13)
  • [42] Durability of concrete exposed to sulfate attack under flexural loading and drying-wetting cycles
    Gao, Jianming
    Yu, Zhenxin
    Song, Luguang
    Wang, Tingxiu
    Wei, Sun
    CONSTRUCTION AND BUILDING MATERIALS, 2013, 39 : 33 - 38
  • [43] Degradation progress of concrete subject to combined sulfate-chloride attack under drying-wetting cycles and flexural loading
    Chen, Fei
    Gao, Jianming
    Qi, Bing
    Shen, Daman
    Li, Luyang
    CONSTRUCTION AND BUILDING MATERIALS, 2017, 151 : 164 - 171
  • [44] Effects of coarse aggregates on chloride diffusion coefficients of concrete and interfacial transition zone under experimental drying-wetting cycles
    Wang, Yuanzhan
    Wu, Linjian
    Wang, Yuchi
    Liu, Chenxi
    Li, Qingmei
    CONSTRUCTION AND BUILDING MATERIALS, 2018, 185 : 230 - 245
  • [45] Chloride Corrosion Process of Concrete with Different Water-Binder Ratios under Variable Temperature Drying-Wetting Cycles
    Wang, Lei
    Chen, Chunhong
    Liu, Ronggui
    Zhu, Pinghua
    Liu, Hui
    Jiang, Hongwei
    Yu, Jiang
    MATERIALS, 2024, 17 (10)
  • [46] Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation
    Ye, Hailong
    Jin, Xianyu
    Fu, Chuanqing
    Jin, Nanguo
    Xu, Yibin
    Huang, Tao
    CONSTRUCTION AND BUILDING MATERIALS, 2016, 112 : 457 - 463
  • [47] Wetting and drying cycles with NaCl solution in model microchannels to understand chloride ion transport in concrete
    Sakai, Y.
    Kishi, T.
    LIFE-CYCLE OF ENGINEERING SYSTEMS: EMPHASIS ON SUSTAINABLE CIVIL INFRASTRUCTURE, 2017, : 873 - 878
  • [48] Chloride ingress behavior of recycled aggregate concrete subjected to sustained compressive loading and drying-wetting cycles
    Bao J.
    Wang Y.
    Mou X.
    Zhang P.
    Yu Z.
    Zhao T.
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2023, 40 (02): : 1015 - 1024
  • [49] Modelling of water and chloride transport in concrete during yearly wetting/drying cycles
    van der Zanden, A. J. J.
    Taher, A.
    Arends, T.
    CONSTRUCTION AND BUILDING MATERIALS, 2015, 81 : 120 - 129
  • [50] Effect of reverse water pressure on chloride penetration within finite concrete during drying-wetting cycles
    Ou, Yangli
    Xu, Meijuan
    Chen, Deqiang
    Jiang, Mingjie
    Xiao, Liang
    Mei, Guoxiong
    Ocean Engineering, 2022, 257
12345