Hot deformation characteristics and microstructure evolution of Hastelloy C-276

被引:72
作者
Jaladurgam, Nitesh Raj [1 ]
Kanjarla, Anand K. [1 ]
机构
[1] Indian Inst Technol Madras, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2018年 / 712卷
关键词
Hastelloy C-276; Dynamic recrystallization; Hot deformation textures; Processing maps; Arrhenius model; HIGH-STRAIN RATE; DYNAMIC RECRYSTALLIZATION; BEHAVIOR; NICKEL; TEXTURE; TEMPERATURE; SUPERALLOY; GRAIN; MECHANISMS; NUCLEATION;
D O I
10.1016/j.msea.2017.11.056
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
High temperature deformation characteristics of Hastelloy C-276 was investigated using compression tests at elevated temperature ranging from 900 degrees C to 1200 degrees C and strain rates covering quasi-static to quasi-dynamic regions (0.001 s(-1)-10 s(-1)) to a final true strain 0.69 (50% Engineering strain). The flow curves at all strain rates and high temperatures (1100 degrees C, 1200 degrees C) exhibit a peak stress, confirming the dynamic recrystallization (DRX) phenomena. To predict and establish the safe hot workability window, processing maps were evaluated based on the dynamic material model and plotted for strain of 0.65. Based on the detailed microstructure analysis and the identification of the active softening mechanisms, the optimal hot workability window was found to be 1200 degrees C and 0.001 s(-1). Bulk texture analysis revealed presence of fiber textures <011> and <001> parallel to deformation axis (ND), which were prevalent at high temperature and low strain rate conditions. Using Arrhenius model, the apparent hot working activation energy (Q(Hw)) was determined as 474 kJ/mol. Zener-Holloman parameter was calculated to gauge the deformation resistance and found to have a linear relationship with peak flow stress at given deformation conditions.
引用
收藏
页码:240 / 254
页数:15
相关论文
共 54 条
[1]  
[Anonymous], 2015, ASM INT
[2]  
[Anonymous], MAT DEPENDENCE DEFOR
[3]  
[Anonymous], CORROSION PERFORMANC
[4]   Dynamic recrystallization mechanisms and twining evolution during hot deformation of Inconel 718 [J].
Azarbarmas, M. ;
Aghaie-Khafri, M. ;
Cabrera, J. M. ;
Calvo, J. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 678 :137-152
[5]   Texture Analysis with MTEX - Free and Open Source Software Toolbox [J].
Bachmann, F. ;
Hielscher, R. ;
Schaeben, H. .
TEXTURE AND ANISOTROPY OF POLYCRYSTALS III, 2010, 160 :63-+
[6]   Dynamic Recrystallization Behavior of Vanadium Micro-alloyed Forging Medium Carbon Steel [J].
Badjena, Sushant Kumar .
ISIJ INTERNATIONAL, 2014, 54 (03) :650-656
[7]   Evolution of Microstructure and Texture During Hot Compression of a Ni-Fe-Cr Superalloy [J].
Coryell, S. P. ;
Findley, K. O. ;
Mataya, M. C. ;
Brown, E. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (02) :633-649
[8]   THE ITERATIVE SERIES-EXPANSION METHOD FOR QUANTITATIVE TEXTURE ANALYSIS .1. GENERAL OUTLINE [J].
DAHMS, M ;
BUNGE, HJ .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1989, 22 :439-447
[9]   A NEW APPROACH IN TEXTURE RESEARCH - LOCAL ORIENTATION DETERMINATION WITH EBSP [J].
ENGLER, O ;
GOTTSTEIN, G .
STEEL RESEARCH, 1992, 63 (09) :413-418
[10]  
GAROFALO F, 1963, T METALL SOC AIME, V227, P351