A novel process for low-density alumina foams

被引：27

作者：

Prabhakaran, K ^{[1
]}

Gokhale, NM ^{[1
]}

Sharma, SC ^{[1
]}

Lal, R ^{[1
]}

机构：

[1] Naval Mat Res Lab, Addl Ambernath 421506, Thane, India

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 2005年 / 88卷 / 09期

关键词：

D O I：

10.1111/j.1551-2916.2005.00446.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A novel process for low-density alumina foams has been studied. Aqueous acidic sucrose solution containing aluminum nitrate when concentrated by heating formed a viscous resin. The resin mixed well with aqueous alumina slurry and the resulting powder-filled resin underwent foaming on heating in a Teflon mold. The green foams produced had very good handling strength. Binder removal and sintering of the green foam prepared at sucrose to alumina weight ratio in the range 0.69-1.03 produced alumina foam bodies with porosities 93.5%-96.7%. Microstructure of the foams depends on sucrose to alumina weight ratio such that a clear transition from reticulated structure to cellular foam structure took place at sucrose to alumina weight ratio below 0.89. Average pore size depends on sucrose to alumina weight ratio and was observed in the range 0.48-2.69 mm.

引用

页码：2600 / 2603

页数：4

共 28 条

[11] Synthesis of macroporous minerals with highly ordered three-dimensional arrays of spheroidal voids
Holland, BT
Blanford, CF
Stein, A
[J]. SCIENCE, 1998, 281 (5376) : 538 - 540
[12] Synthesis of highly ordered, three-dimensional, macroporous structures of amorphous or crystalline inorganic oxides, phosphates, and hybrid composites
Holland, BT
Blanford, CF
Do, T
Stein, A
[J]. CHEMISTRY OF MATERIALS, 1999, 11 (03) : 795 - 805
[13] Coated polystyrene particles as templates for ordered macroporous silica structures with controlled wall thickness
Hotta, Y
Alberius, PCA
Bergström, L
[J]. JOURNAL OF MATERIALS CHEMISTRY, 2003, 13 (03) : 496 - 501
[14] Microstructure, permeability and mechanical behaviour of ceramic foams
Lopes, RA
Segadaes, AM
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 209 (1-2): : 149 - 155
[15] Processing of porous ceramics by 'starch consolidation'
Lyckfeldt, O
Ferreira, JMF
[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1998, 18 (02) : 131 - 140
[16] MYERS D, 1999, SURF INTERFACES, P214
[17] PIGMAN W, 1957, CARBOHYDRATES, P59
[18] Sucrose combustion synthesis of LaxSr(1-x)MnO3 (x ≤ 0.2) powders
Prabhakaran, K
Joseph, J
Gokhale, NM
Sharma, SC
Lal, R
[J]. CERAMICS INTERNATIONAL, 2005, 31 (02) : 327 - 331
[19] REED JS, 1995, PRINICPLES CERAMICS, P186
[20] SAGGIOWOYANSKY J, 1992, AM CERAM SOC BULL, V71, P1674

← 1 2 3 →