Crack Initiation Mechanism and Life Prediction of Ti60 Titanium Alloy Considering Stress Ratios Effect in Very High Cycle Fatigue Regime

被引：7
|
作者：
He, Ruixiang [1 ,2 ]
Peng, Haotian [1 ,2 ]
Liu, Fulin [1 ,2 ]
Khan, Muhammad Kashif [3 ]
Chen, Yao [1 ,2 ]
He, Chao [1 ,2 ]
Wang, Chong [1 ,2 ]
Wang, Qingyuan [1 ,2 ]
Liu, Yongjie [1 ,2 ]
机构：
[1] Sichuan Univ, Failure Mech & Engn Disaster Prevent Key Lab Sich, Chengdu 610207, Peoples R China
[2] Sichuan Univ, Coll Architecture & Environm, MOE Key Lab Deep Earth Sci & Engn, Chengdu 610065, Peoples R China
[3] Coventry Univ, Inst Future Transport & Cities, Coventry CV1 5FB, W Midlands, England
来源：
MATERIALS | 2022年 / 15卷 / 08期
关键词：
very high cycle fatigue; Ti60 titanium alloy; fatigue failure mechanism; fatigue life prediction; fatigue strength prediction; stress ratio; CHROMIUM-BEARING STEEL; DEFORMATION-BEHAVIOR; FAILURE-MECHANISM; PROPAGATION; VARIABILITY; MICROSTRUCTURE; NUCLEATION; PROPERTY; JOINT;
D O I：
10.3390/ma15082800
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Ultrasonic fatigue tests were performed on Ti60 titanium alloy up to a very high cycle fatigue (VHCF) regime at various stress ratios to investigate the characteristics. The S-N curves showed continuous declining trends with fatigue limits of 400, 144 and 130 MPa at 10(9) cycles corresponding to stress ratios of R = -1, 0.1 and 0.3, respectively. Fatigue cracks found to be initiated from the subsurface of the specimens in the VHCF regime, especially at high stress ratios. Two modified fatigue life prediction models based on fatigue crack initiation mechanisms for Ti60 titanium alloy in the VHCF regime were developed which showed good agreement with the experimental data.
引用
收藏
页数：15
相关论文
共 50 条
  • [1] Fracture mechanism of Ti60 alloy at high temperature in very high cycle fatigue regime and fatigue life prediction
    Zhou, Qikai
    Huang, Zhiyong
    Qian, Hongjiang
    Wang, Jian
    Shen, Zeshuai
    Pan, Kai
    Chen, Yonghui
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (09) : 3285 - 3299
  • [2] Crack initiation mechanism of titanium alloy in very high cycle fatigue regime at 400℃ considering stress ratio effect
    Liu, Fulin
    Peng, Haotian
    Liu, Yongjie
    Wang, Chong
    Wang, Qingyuan
    Chen, Yao
    International Journal of Fatigue, 2022, 163
  • [3] Crack initiation mechanism of titanium alloy in very high cycle fatigue regime at 400°C considering stress ratio effect
    Liu, Fulin
    Peng, Haotian
    Liu, Yongjie
    Wang, Chong
    Wang, Qingyuan
    Chen, Yao
    INTERNATIONAL JOURNAL OF FATIGUE, 2022, 163
  • [4] Multiaxial fatigue life prediction based on effective factor with shear/axial stress ratio for Ti60 titanium alloy in very high cycle regime
    Chen, Chao -Lin
    Shang, De-Guang
    Xiao, Na-Min
    Li, Xing -Wu
    Sha, Ai-Xue
    Li, Jing
    Li, Jing-Xuan
    Tang, Zhi-Qiang
    Han, Zhao-Yun
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 184
  • [5] Fatigue life prediction of Ti60 titanium alloy under very high cycle loading at different temperatures
    Chen, Chao -Lin
    Shang, De-Guang
    Xiao, Na-Min
    Li, Xing -Wu
    Sha, Ai-Xue
    Li, Jing
    Li, Jing-Xuan
    Tang, Zhi-Qiang
    Han, Zhao-Yun
    Guo, Yi-Er
    Li, Dao-Hang
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
  • [6] Very high cycle fatigue life prediction of Ti60 alloy based on machine learning with data enhancement
    Qian, Hongjiang
    Huang, Zhiyong
    Xu, Yeting
    Zhou, Qikai
    Wang, Jian
    Shen, Jiebin
    Shen, Zeshuai
    ENGINEERING FRACTURE MECHANICS, 2023, 289
  • [7] Faceted crack initiation characteristics for high-cycle and very-high-cycle fatigue of a titanium alloy under different stress ratios
    Liu, Xiaolong
    Sun, Chengqi
    Hong, Youshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 92 : 434 - 441
  • [8] Fatigue failure mechanism of Ti60 titanium alloy in HCF and VHCF regime at different temperatures
    Chen, Chao -Lin
    Shang, De-Guang
    Tang, Zhi-Qiang
    Li, Dao-Hang
    Yin, Xiang
    Guo, Yi-Er
    ENGINEERING FAILURE ANALYSIS, 2023, 151
  • [9] Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime
    Qin, Zhi
    Li, Bin
    Chen, Chen
    Chen, Tianyue
    Chen, Rui
    Zhang, Han
    Xue, Hongqian
    Yao, Changfeng
    Tan, Liang
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 26 : 720 - 736
  • [10] Crack initiation mechanism of extruded AZ31 magnesium alloy in the very high cycle fatigue regime
    Yang, F.
    Yin, S. M.
    Li, S. X.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 491 (1-2): : 131 - 136
12345