Influences of the quantity of Mg2Sn phase on the corrosion behavior of Mg-7Sn magnesium alloy

被引：144

作者：

Liu, Xianbin ^{[1
]}

Shan, Dayong ^{[1
]}

Song, Yingwei ^{[1
]}

Chen, Rongshi ^{[1
]}

Han, Enhou ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Liaoning, Peoples R China

来源：

ELECTROCHIMICA ACTA | 2011年 / 56卷 / 05期

关键词：

Mg2Sn phase; Mg-7Sn alloy; Corrosion mode; Solution temperature; Stannic oxide; SN; AZ91; MICROSTRUCTURE; ZN;

D O I：

10.1016/j.electacta.2010.12.030

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The influence of the quantity of the Mg2Sn phase on the corrosion behavior of different solution temperature treated Mg-7Sn magnesium alloy has been investigated by electrochemical measurements, scanning electron microscope (SEM) observation, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) analysis. With the increase of solution temperature, the quantity of Mg2Sn phase decreased and the tin concentration of matrix increased. The dissolved tin in Mg matrix took part in the film formation and the constituent of film was magnesium oxide and stannic oxide. The corrosion mode and corrosion rate were associated with the quantity of Mg2Sn phases and tin concentration of the matrix. If most of tin was present as Mg2Sn, the corrosion mode was pitting corrosion and it accelerated the corrosion rate. If most of tin was dissolved in matrix, the corrosion mode was filiform corrosion and it decreased the corrosion rate. The experiment evidences demonstrated that the corrosion resistance can be improved by increasing the tin concentration of matrix and the lowest corrosion rate was observed for sample solution treated at 540 degrees C. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：2582 / 2590

页数：9

共 23 条

[1] Microstructure and corrosion behavior of Mg-Sn-Ca alloys after extrusion [J].

Abu Leil, T. ;

Hort, N. ;

Dietzel, W. ;

Blawert, C. ;

Huang, Y. ;

Kainer, K. U. ;

Rao, K. P. .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2009, 19 (01) :40-44

[2]

[Anonymous], CHEM NUCL MAT

[3] In situ observation of pit initiation of passivated AZ91 magnesium alloy [J].

Chen, Jian ;

Wang, Jianqiu ;

Han, En-Hou ;

Ke, Wei .

CORROSION SCIENCE, 2009, 51 (03) :477-484

[4] Effect of magnesium hydride on the corrosion behavior of an AZ91 magnesium alloy in sodium chloride solution [J].

Chen, Jian ;

Dong, Junhua ;

Wang, Jianqiu ;

Han, Enhou ;

Ke, Wei .

CORROSION SCIENCE, 2008, 50 (12) :3610-3614

[5] Microstructure and mechanical properties of binary Mg-Sn alloys subjected to indirect extrusion [J].

Cheng, W. L. ;

Park, S. S. ;

You, B. S. ;

Koo, B. H. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (18-19) :4650-4653

[6] Comparison of corrosion behaviors of AZ31, AZ91, AM60 and ZK60 magnesium alloys [J].

Cheng Ying-liang ;

Qin Ting-wei ;

Wang Hui-min ;

Zhang Zhao .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2009, 19 (03) :517-524

[7] Improvement in stannate chemical conversion coatings on AZ91 D magnesium alloy using the potentiostatic technique [J].

Elsentriecy, Hassan H. ;

Azumi, Kazuhisa ;

Konno, Hidetaka .

ELECTROCHIMICA ACTA, 2007, 53 (02) :1006-1012

[8] Correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys [J].

Feliu, S., Jr. ;

Pardo, A. ;

Merino, M. C. ;

Coy, A. E. ;

Viejo, F. ;

Arrabal, R. .

APPLIED SURFACE SCIENCE, 2009, 255 (07) :4102-4108

[9] Microstructural investigations of the Mg-Sn-xCa system [J].

Hort, Norbert ;

Huang, Ybanding ;

Abu Leil, Torek ;

Maier, Petra ;

Kainer, Karl Ulrich .

ADVANCED ENGINEERING MATERIALS, 2006, 8 (05) :359-364

[10]

Li M.S., 2001, High Temperature Corrosion of Metal [M]

← 1 2 3 →