Processing maps for hot deformation of rolled AZ31 magnesium alloy plate: Anisotropy of hot workability

被引:162
作者
Prasad, Y. V. R. K. [1 ]
Rao, K. P. [1 ]
机构
[1] City Univ Hong Kong, Dept Mfg Engn & Engn Management, Kowloon, Hong Kong, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 487卷 / 1-2期
关键词
processing maps; magnesium alloy; hot deformation; texture; dynamic recrystallization; pyramidal slip;
D O I
10.1016/j.msea.2007.10.038
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Processing maps on rolled AZ31 magnesium plate have been developed in the range 300-550 degrees C and 0.0003-10s(-1) by hot compression of specimens parallel to the rolling direction (RD), the transverse direction (TD), or the normal direction (ND) with a view to examine whether the hot workability is anisotropic. The processing map for RD specimens exhibited a single wide domain of workability in the temperature range 350-550 degrees C and strain rate range 0.0003-0.3 s(-1) in which dynamic recrystallization (DRX) occurs. The apparent activation energy in this domain is estimated to be 143 kJ/mole, which is close to that for self-diffusion in magnesium. On the other hand, the maps for the TD and ND specimens exhibited two DRX domains, one at lower strain rates (0.01 s(-1)) and the other at higher strain rates (>1 s(-1)). The apparent activation energies estimated in the lower strain rate DRX domain of TD and ND maps are 180 and 168 kJ/mole, respectively, suggesting cross-slip occurs in this domain. In the higher strain rate domain, the apparent activation energy estimated in both TD and ND specimens is 105 kJ/mole, which is close to that for grain-boundary diffusion. The results suggest that the hot deformation behavior is anisotropic and a simple correlation with the known primary rotting texture ({0 0 0 2} < 10 (1) over bar 0 >) revealed that both the first order and second order pyramidal slip systems are favored in the RD orientation resulting in higher workability. The other two orientations may be considered "harder" as regards hot workability since either the first order or the second order pyramidal slip is likely to dominate. In all the three orientations and within the DRX domains, the grain size varies linearly with the Zener-Hollomon parameter. (c) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码:316 / 327
页数:12
相关论文
共 59 条
[11]   Enhanced formability at elevated temperature of a cross-rolled magnesium alloy sheet [J].
Chino, Yasumasa ;
Sassa, Kensuke ;
Kamiya, Akira ;
Mabuchi, Mamoru .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 441 (1-2) :349-356
[12]   Texture evolution during large-strain hot rolling of the Mg AZ61 alloy [J].
del Valle, JA ;
Pérez-Prado, MT ;
Ruano, OA .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 355 (1-2) :68-78
[13]   Sheet metal forming of magnesium wrought alloys -: formability and process technology [J].
Doege, E ;
Dröder, K .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2001, 115 (01) :14-19
[14]   Enhancement of workability in AZ31 alloy-processing maps: Part I, cast material [J].
Dzwonczyk, Joanna ;
Prasad, Yellapregada Venkata Rama Krishna ;
Hort, Norbert ;
Kainer, Karl Ulrich .
ADVANCED ENGINEERING MATERIALS, 2006, 8 (10) :966-973
[15]  
Frost H.J., 1982, Deformation Mechanism Maps, P44
[16]   Texture effects on plastic deformation of magnesium [J].
Gehrmann, R ;
Frommert, MM ;
Gottstein, G .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 395 (1-2) :338-349
[17]   Microstructure evolution and texture development during high-temperature uniaxial compression of magnesium alloy AZ31 [J].
Helis, Libor ;
Okayasu, Kazuto ;
Fukutomi, Hiroshi .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 430 (1-2) :98-103
[18]  
Hilborn RC., 1994, CHAOS NONLINEAR DYNA
[19]   Basal-texture induced low formability during room temperature hydroforming of fine-grained AZ31 Mg tubes [J].
Huang, CC ;
Huang, JC ;
Lin, YK ;
Hwang, YM .
MATERIALS TRANSACTIONS, 2004, 45 (11) :3142-3149
[20]   Improvement of formability from room temperature to warm temperature in AZ-31 magnesium alloy [J].
Iwanaga, K ;
Tashiro, H ;
Okamoto, H ;
Shimizu, K .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 155 :1313-1316