Optimisation of the mechanical properties of a new PM superalloy for disk applications

被引：0

作者：

Locq, D ^{[1
]}

Marty, M ^{[1
]}

Caron, P ^{[1
]}

机构：

[1] Off Natl Etud & Rech Aerosp, F-92322 Chatillon, France

来源：

SUPERALLOYS 2000 | 2000年

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The roles of the subsolvus solutioning temperature and of the ageing temperature on the microstructure and on tensile and creep properties were evaluated on a new PM superalloy, designated NR3. A single-stage ageing treatment was applied instead of the usual double-stage ageing treatment. The principal objective was to improve the creep resistance of this superalloy while keeping a high tensile strength by using a simplified heat treatment. The solution treatment essentially affected the respective proportions of primary and secondary gamma' precipitates and the grain size. On the other hand, the major influence of the increase of the ageing temperature was to coarsen the tertiary gamma' particles. These microstructural effects were successfully combined to obtained a significant increase of the creep strength associated with a slight rise of the tensile properties.

引用

页码：395 / 403

页数：9

共 16 条

[11]

Morinaga M., 1984, SUP 1984 5 INT S TMS, P523, DOI [10.7449/1984/Superalloys_1984_523_532, DOI 10.7449/1984/SUPERALLOYS_1984_523_532]

[12] SOME NEW ASPECTS CONCERNING PARTICLE HARDENING MECHANISMS IN GAMMA' PRECIPITATING NI-BASE ALLOYS .1. THEORETICAL CONCEPT [J].

REPPICH, B .

ACTA METALLURGICA, 1982, 30 (01) :87-94

[13]

WALDER A, 1988, 16 C INT COUNC AER S

[14]

WATANABE R, 1976, T IRON STEEL I JPN, V16, P437

[15]

Wlodek ST, 1996, SUPERALLOYS 1996, P129, DOI 10.7449/1996/Superalloys_1996_129_136

[16]

WLODEK ST, 1992, SUPERALLOYS 1992, P467

← 1 2 →