Effects of Ta2O5 content on mechanical properties and high-temperature performance of Zr6Ta2O17 thermal barrier coatings

被引：21
|
作者：
Liu, Qing [1 ,2 ]
Hu, Xiaopeng [1 ,2 ]
Zhu, Wang [1 ,2 ]
Guo, Jinwei [1 ,2 ]
Tan, Zhenyu [1 ,2 ]
机构：
[1] Xiangtan Univ, Sch Mat Sci & Engn, Key Lab Key Film Mat & Applicat Equipment Hunan P, Xiangtan 411105, Hunan, Peoples R China
[2] Xiangtan Univ, Sch Mat Sci & Engn, Minist Educ, Key Lab Low Dimens Mat & Applicat Technol, Xiangtan, Hunan, Peoples R China
来源：
JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 2021年 / 104卷 / 12期
关键词：
elastic modulus; fracture toughness; hardness; high-temperature performance; Ta2O5; content; Zr6Ta2O17; coating; PHASE-STABILITY; CERAMIC-LAYER; CONDUCTIVITY; BEHAVIOR;
D O I：
10.1111/jace.17990
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Zr6Ta2O17/YSZ double ceramic top coat thermal barrier coatings (TBCs) with different Ta2O5 content are prepared by atmospheric plasma spraying (APS). The effects of Ta2O5 content on mechanical properties and high-temperature performance of Zr6Ta2O17 TBCs are investigated. With the decrease in Ta2O5 content, the hardness and fracture toughness of the Zr6Ta2O17 coating increases from 12.833 to 15.117 GPa and from 3.3592 to 3.7753 MPa m(1/2), respectively. The Zr6Ta2O17 coating specimens with different Ta2O5 content do not delaminate from the substrate except the edge peeling after 180 h of oxidation or 2000 thermal cycles at 1150 degrees C. The Zr-12Ta specimen (the molar ratio of ZrO2/Ta2O5 of 0.88:0.12) presents the more excellent mechanical properties and high-temperature performance. The reduction in Ta2O5 content will improve the mechanical properties, high-temperature oxidation, and thermal cycle performance of Zr6Ta2O17/YSZ double ceramic top coat TBCs.
引用
收藏
页码：6533 / 6544
页数：12
相关论文
共 50 条
  • [1] Effect of microstructure on the performance of Zr6Ta2O17 ceramics as thermal barrier coatings
    Tan, Z. Y.
    Yan, G.
    Cao, K.
    Cheng, C. Y.
    Yang, L.
    Zhou, Y. C.
    CERAMICS INTERNATIONAL, 2023, 49 (18) : 29449 - 29458
  • [2] Thermal and mechanical properties of Ta2O5 doped La2Ce2O7 thermal barrier coatings prepared by atmospheric plasma spraying
    Zhang, Hao
    Su, Junbin
    Duo, Shuwang
    Zhou, Xin
    Yuan, Jieyan
    Dong, Shujuan
    Yang, Xiong
    Zeng, Jinyan
    Jiang, Jianing
    Deng, Longhui
    Cao, Xueqiang
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2019, 39 (07) : 2379 - 2388
  • [3] Study on properties of Hf6Ta2O17/Ta2O5 system: A potential candidate for environmental barrier coating (EBC)
    Li, Hao
    Yu, Yiping
    Fang, Bing
    Xiao, Peng
    Wang, Song
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2022, 42 (11) : 4651 - 4662
  • [4] High-temperature compressive creep behavior and mechanism of Hf6Ta2O17 ceramic as a candidate for thermal barrier coatings
    Zheng, Y. X.
    Hu, X. P.
    Liu, S.
    Liu, Q.
    Zou, Y.
    Guo, J. W.
    Zhu, W.
    CERAMICS INTERNATIONAL, 2023, 49 (18) : 29905 - 29912
  • [5] Effect of HfO2 content on CMAS corrosion resistance of a promising Hf6Ta2O17 ceramic for thermal barrier coatings
    Liu, S.
    Hu, X. P.
    Liu, Q.
    Guo, J. W.
    Wu, J. Y.
    Zhu, W.
    CORROSION SCIENCE, 2022, 208
  • [6] Elinvar-Like Effect Induced by High Lattice Distortion in Zr6Ta2O17 Ceramics
    Hu, Xiaopeng
    Liu, Qing
    Liu, Sai
    Zou, Yu
    Guo, Jinwei
    Wu, Junyao
    Zhu, Wang
    Ma, Zengsheng
    RESEARCH, 2024, 7
  • [7] Mechanical properties and thermal cycling behavior of Ta2O5 doped La2Ce2O7 thermal barrier coatings prepared by atmospheric plasma spraying
    Zhang, Hao
    Wang, Jinshuang
    Dong, Shujuan
    Yuan, Jieyan
    Zhou, XinR
    Duo, Shuwang
    Chen, Si
    Huo, Panjie
    Jiang, Jianing
    Deng, Longhui
    Cao, Xueqiang
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 785 : 1068 - 1076
  • [8] Mechanical properties of Nb2O5 and Ta2O5 prepared by different procedures
    O. B. Shcherbina
    M. N. Palatnikov
    V. V. Efremov
    Inorganic Materials, 2012, 48 : 433 - 438
  • [9] Mechanical properties of Nb2O5 and Ta2O5 prepared by different procedures
    Shcherbina, O. B.
    Palatnikov, M. N.
    Efremov, V. V.
    INORGANIC MATERIALS, 2012, 48 (04) : 433 - 438
  • [10] Mechanical properties and calcium-magnesium-alumino-silicate (CMAS) corrosion behavior of a promising Hf6Ta2O17 ceramic for thermal barrier coatings
    Tan Z.Y.
    Yang Z.H.
    Zhu W.
    Yang L.
    Zhou Y.C.
    Hu X.P.
    Ceramics International, 2020, 46 (16) : 25242 - 25248
12345