Effect of frequency on very high cycle fatigue behavior of a low strength Cr-Ni-Mo-V steel welded joint

被引：52
|
作者：
Zhu, Ming-Liang [1 ]
Liu, Long-Long [1 ]
Xuan, Fu-Zhen [1 ]
机构：
[1] E China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2015年 / 77卷
基金：
中国国家自然科学基金; 上海市自然科学基金;
关键词：
Very high cycle fatigue; Loading frequency; Welded joint; Fatigue crack initiation; Fracture location; LOADING FREQUENCY; LOW-CARBON; CRACK INITIATION; BEARING STEEL; PROPAGATION; MECHANISM; MICROSTRUCTURE; DEFORMATION; NIOBIUM; ALLOYS;
D O I：
10.1016/j.ijfatigue.2015.03.027
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Axially fully-reversed fatigue test of a low strength Cr-Ni-Mo-V steel welded joint was conducted up to the very high cycle fatigue regime under the frequency of 110 Hz and 20 kHz. The S-N curve shows a duplex shape at low frequency while decreases continuously at high frequency. Sites of crack initiation and fracture of the welds depend on stress level and loading frequency, hence leading to changed fatigue strength. In addition, frequency effect varies among different parts of the welded joint and fatigue lifetime. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：166 / 173
页数：8
相关论文
共 50 条
  • [41] Very high cycle fatigue properties of Cr-Mo low alloy steel containing V-rich MC type carbides
    Hui, Weijun
    Zhang, Yongjian
    Zhao, Xiaoli
    Zhou, Chao
    Wang, Kaizhong
    Sun, Wei
    Dong, Han
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 651 : 311 - 320
  • [42] EFFECT OF HYDROSTATIC PRESSURE AND PRESTRESS ON CORROSION BEHAVIOR OF A NEW TYPE Ni-Cr-Mo-V HIGH STRENGTH STEEL
    Fan Lin
    Ding Kangkang
    Guo Weimin
    Zhang Penghui
    Xu Likun
    ACTA METALLURGICA SINICA, 2016, 52 (06) : 679 - 688
  • [43] Microstructure and Mechanical Properties of Welded Joint of a Fe-Cr-Ni-Mo Steel with High-Strength and High-Toughness
    Hu Xiaofeng
    Jiang Haichang
    Zhao Mingjiu
    Yan Desheng
    Lu Shanping
    Rong Lijian
    ACTA METALLURGICA SINICA, 2018, 54 (01) : 1 - 10
  • [44] High Cycle Fatigue Properties and Failure Mode in Ni-Cr-Mo steel Tempered at Low Temperature
    Mochizuki, Yu
    Nakajima, Masaki
    Shimizu, Toshihiro
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VII, 2008, 385-387 : 185 - +
  • [45] Effect of hydrostatic pressure on the corrosion behaviour of Ni-Cr-Mo-V high strength steel
    Yang, Yange
    Zhang, Tao
    Shao, Yawei
    Meng, Guozhe
    Wang, Fuhui
    CORROSION SCIENCE, 2010, 52 (08) : 2697 - 2706
  • [46] The effect of microstructure on the fatigue crack growth behavior of Ni-Cr-Mo-V steel weld metal
    Han, Chaoyu
    Liu, Qu
    Cai, Zhipeng
    Sun, Qixing
    Huo, Xin
    Fan, Manjie
    Li, Kejian
    Pan, Jiluan
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
  • [47] EFFECT OF HARDENABILITY ON RESISTANCE OF CR-NI-MO-V STEELS TO BRITTLE-FRACTURE
    KRAMAROV, MA
    RYBAKOV, AB
    SHAKHNAZ.YV
    STEEL IN THE USSR, 1973, 3 (02): : 156 - 157
  • [48] Hot Deformation Behavior and Dynamic Recrystallization Characteristics in a Low-Alloy High-Strength Ni–Cr–Mo–V Steel
    Chuan Wu
    Shuang Han
    Acta Metallurgica Sinica (English Letters), 2018, 31 : 963 - 974
  • [49] Hot Deformation Behavior and Dynamic Recrystallization Characteristics in a Low-Alloy High-Strength Ni–Cr–Mo–V Steel
    Chuan Wu
    Shuang Han
    Acta Metallurgica Sinica(English Letters), 2018, 31 (09) : 963 - 974
  • [50] STRAIN WAVE SHAPE AND FREQUENCY-EFFECTS ON THE HIGH-TEMPERATURE, LOW-CYCLE FATIGUE BEHAVIOR OF A 1CR-MO-V FERRITIC STEEL
    MELTON, KN
    MATERIALS SCIENCE AND ENGINEERING, 1982, 55 (01): : 21 - 28
12345