Microstructure and mechanical properties of pulsed electric current sintered B4C-TiB2 composites

Monolithic B4C, TiB2 and B4C-TiB2 particulate composites were consolidated without sintering additives by means of pulsed electric current sintering in vacuum. Sintering studies on B4C-TiB2 composites were carried out to reveal the influence of the pressure loading cycle during pulsed electrical current sintering (PECS) on the removal of oxide impurities, i.e. boron oxide and titanium oxide, hereby influencing the densification behavior as well as microstructure evolvement. The critical temperature to evaporate the boron oxide impurities was determined to be 2000 degrees C. Fully dense B4C-TiB2 composites were achieved by PECS for 4 min at 2000 degrees C when applying the maximum external pressure of 60 MPa after volatilization of the oxide impurities, whereas a relative density of 95-97% was obtained when applying the external pressure below 2000 degrees C. Microstructural analysis showed that B4C and TiB2 grain growth was substantially suppressed due to the pinning effect of the secondary phase and the rapid sintering cycle, resulting in micrometer sized and homogeneous microstructures. Excellent properties were obtained for the 60 vol% TiB2 composite, combining a Vickers hardness of 29 GPa, a fracture toughness of 4.5 MPa m(1/2) and a flexural strength of 867 MPa, as well as electrical conductivity of 3.39E+6S/m. (C) 2010 Elsevier B.V. All rights reserved.