Characterization of the Effect of the CO2/CO Sintering Atmosphere on the Abrasion Resistance of a FeCrCB Hardfacing Coating

被引：0

作者：

Valenzuela-De la Rosa, Fernando ^{[1
]}

Torres-Sanchez, Roal ^{[1
]}

Dominguez-Rios, Carlos ^{[1
]}

Aguilar-Elguezabal, Alfredo ^{[1
]}

机构：

[1] Adv Mat Res Ctr SC, Natl Nanotechnol Lab, Chihuahua 31136, Chihuahua, Mexico

来源：

METALS | 2021年 / 11卷 / 10期

关键词：

abrasion; slurry; sintering; tape casting; CO2/CO atmosphere; hardfacing; WEAR-RESISTANCE; BEHAVIOR; MICROSTRUCTURE; STEEL; ALLOY; HARDNESS;

D O I：

10.3390/met11101568

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

FeCrCB alloys have become an attractive option as a hardfacing coating to extend the service life of tools used in primary and secondary industries. In this work, experiments are reported on the sintering of FeCrCB alloy powders for hardfacing coatings by modifying the CO2/CO ratio using six different atmospheric gas conditions. The hardfacing coating was found to have higher microhardness and higher abrasion resistance under a 10C atmosphere. This increase in mechanical properties is related to the microstructure, as the atmosphere using 10C promotes the formation of a higher quantity of hard phases, while the presence of CO induces the formation of higher volumetric fractions of eutectic phases, and, consequently, lower abrasion resistance is obtained.</p>

引用

页数：13

共 34 条

[1]

[Anonymous], TECHNICAL REPORT LIN

[2]

[Anonymous], 2000, G65 ASTM INT

[3]

Badisch E., 2008, Tribotest, V14, P225, DOI 10.1002/tt.61

[4] MICROSTRUCTURE OF FE-CR-C HARDFACING ALLOYS WITH ADDITIONS OF NB, TI AND, B [J].

BERNS, H ;

FISCHER, A .

METALLOGRAPHY, 1987, 20 (04) :401-429

[5] ABRASIVE WEAR-RESISTANCE AND MICROSTRUCTURE OF FE-CR-C-B HARD SURFACING WELD DEPOSITS [J].

BERNS, H ;

FISCHER, A .

WEAR, 1986, 112 (02) :163-180

[6] Effect of particle hardness on mild-severe wear transition of hard second phase materials [J].

Coronado, J. J. ;

Rodriguez, S. A. ;

Sinatora, A. .

WEAR, 2013, 301 (1-2) :82-88

[7] Low stress abrasive wear behavior of a hardfaced steel [J].

Dasgupta, R ;

Prasad, BK ;

Jha, AK ;

Modi, OP ;

Das, S ;

Yegneswaran, AH .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1998, 7 (02) :221-226

[8]

De la Rosa FV, 2020, J Miner Mater Charact Eng, V8, P393

[9]

Fridman G.L, 1970, POROSHKOVAYA METALL, V7, P82, DOI [10.1007/BF00823616, DOI 10.1007/BF00823616]

[10] Influence of Sintering under Nitrogen Atmosphere on Microstructures of Powder Metallurgy Duplex Stainless Steels [J].

Garcia, C. ;

Martin, F. ;

Blanco, Y. ;

De Tiedra, M. P. ;

Aparicio, M. L. .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (02) :292-301

← 1 2 3 4 →