Creep Behavior of High Density Polyethylene after Aging in Contact with Different Oil Derivates

被引:17
作者
Habas-Ulloa, Amelia [2 ]
D'Almeida, Jose-Roberto Moraes [2 ]
Habas, Jean-Pierre [1 ]
机构
[1] Univ Montpellier 2, Equipe Ingn & Architectures Macromol, CNRS UM2 ENSCM UM1, Inst Charles Gerhardt Montpellier,UMR5253, F-34095 Montpellier 5, France
[2] Dept Mat Sci & Met, BR-22453900 Rio De Janeiro, Brazil
关键词
SLOW CRACK-GROWTH; MECHANICAL-PROPERTIES; BIMODAL POLYETHYLENE; MOLECULAR-WEIGHT; FUEL-OIL; HDPE; STRESS; PIPES; PLASTICIZATION; POLYPROPYLENE;
D O I
10.1002/pen.21743
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The creep behavior of a high density polyethylene (HDPE), currently used as raw material for pipe manufacture, was evaluated before and after exposure to oil derivates using transient rheometry. The creep behavior of the original HDPE was satisfactorily described using a generalized Kelvin-Voigt model based on two retardation times. The values of these critical times were quite different from each other, indicating a large distribution of macromolecular weight. The aging procedure was performed by immersing the polymer in two model fluids chosen to discriminate and understand the action of aromatic and paraffinic fractions of fuel derivatives (white oil, gas-oil). The batch operation was also carried out at two different temperatures to investigate the thermal activation of plausible degrading mechanisms. In the case of the aging performed in the paraffinic fluid, the polymer compliance continuously increased with the immersion duration. This behavior was attributed to a plasticization induced by the diffusion of the liquid in the polymer matrix. The same phenomenon was observed in the early stage of the HDPE aging carried out with the aromatic fluid. However, for longer aging times, the extraction of low molecular weight species produced the stiffening of the thermoplastic. POLYM. ENG. SCI., 50:2122-2130, 2010. (C) 2010 Society of Plastics Engineers
引用
收藏
页码:2122 / 2130
页数:9
相关论文
共 31 条
[1]  
Alt FP, 2001, MACROMOL SYMP, V163, P135, DOI 10.1002/1521-3900(200101)163:1<135::AID-MASY135>3.0.CO
[2]  
2-7
[3]  
Barnes H. A., 1989, An introduction to rheology, V3, P37
[4]   Modelling of creep behaviour in injection-moulded HDPE [J].
Beijer, JGJ ;
Spoormaker, JL .
POLYMER, 2000, 41 (14) :5443-5449
[5]   Failure prediction analysis for polyethylene flawed pipes [J].
Bernal, C ;
Montenegro, HL ;
Frontini, P .
ENGINEERING FRACTURE MECHANICS, 2003, 70 (15) :2149-2162
[6]   Morphology and dynamic mechanical properties of high density polyethylene/petroleum resin/polyethylene-octylene elastomer blends [J].
Cao, Deming ;
Cao, Yuanyi ;
Wu, Chifei .
POLYMER BULLETIN, 2009, 63 (01) :57-67
[7]   Experimental and theoretical investigation of stress corrosion crack (SCC) growth of polyethylene pipes [J].
Choi, Byoung-Ho ;
Chudnovsky, Alexander ;
Paradkar, Raiesh ;
Michie, William ;
Zhou, Zhenwen ;
Cham, Pak-Meng .
POLYMER DEGRADATION AND STABILITY, 2009, 94 (05) :859-867
[8]   Effects of cyclic stress and insulation on the corrosion fatigue properties of thermally insulated pipeline [J].
Choi, YS ;
Chung, MK ;
Kim, JG .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 384 (1-2) :47-56
[9]   Characterization of the Microstructure of Bimodal HDPE Resin [J].
Fan, Yandi ;
Xue, Yanhu ;
Nie, Wei ;
Ji, Xiangling ;
Bo, Shuqin .
POLYMER JOURNAL, 2009, 41 (08) :622-628
[10]  
Ferry J. D., 1980, VISCOELASTIC PROPERT, P37