Time dependence and service life prediction of chloride resistance of concrete coatings

被引：40

作者：

Li, Guo ^{[1
]}

Yang, Boyuan ^{[1
]}

Guo, Changsheng ^{[1
]}

Du, Jianmin ^{[1
]}

Wu, Xiaosuo ^{[1
]}

机构：

[1] China Univ Min & Technol, Jiangsu Key Lab Environm Impact & Struct Safety E, Xuzhou 221116, Peoples R China

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2015年 / 83卷

关键词：

Concrete coating; Chloride resistance; Time dependence; Coulomb electric flux; SURFACE-COATINGS; DURABILITY; CORROSION; PERFORMANCE; MORTAR; WATER;

D O I：

10.1016/j.conbuildmat.2015.03.003

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This study aims to determine the effects of coating category and degradation on chloride resistance and service life of concrete coatings. Four typical coatings were applied on concrete specimens, and aged under outdoor natural climate conditions and indoor artificial accelerated experiments using ultraviolet light radiation and wetting/drying cycle. Coulomb electric fluxes of the specimens were periodically tested to determine their chloride resistance before and during aging. The chloride resistance of concrete is remarkably improved with the use of coatings, and organic film coatings provide superior improvement to infiltrating coatings. The chloride resistance of coatings is time-dependent, and organic film coatings exhibit faster aging than infiltrating coatings. The experimental time needed for coating degradation can be shortened through artificial accelerated aging experiments. The service lives of concrete coatings against chloride resistance are closely related and can be predicted through sunlight irradiance of the service environment. (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：19 / 25

页数：7

共 23 条

[1] Effect of waterproofing coatings on steel reinforcement corrosion and physical properties of concrete [J].

Al-Zahrani, MM ;

Al-Dulaijan, SU ;

Ibrahim, M ;

Saricimen, H ;

Sharif, FM .

CEMENT & CONCRETE COMPOSITES, 2002, 24 (01) :127-137

[2] Effectiveness of surface coatings in improving concrete durability [J].

Almusallam, AA ;

Khan, FM ;

Dulaijan, SU ;

Al-Amoudi, OSB .

CEMENT & CONCRETE COMPOSITES, 2003, 25 (4-5) :473-481

[3]

[Anonymous], 1997, C1202 ASTM

[4] Long-term chloride-induced corrosion monitoring of reinforced concrete coated with commercial polymer-modified mortar and polymeric coatings [J].

Brenna, A. ;

Bolzoni, F. ;

Beretta, S. ;

Ormellese, M. .

CONSTRUCTION AND BUILDING MATERIALS, 2013, 48 :734-744

[5] Effect of polymer modified cementitious coatings on water and chloride permeability in concrete [J].

Diamanti, M. V. ;

Brenna, A. ;

Bolzoni, F. ;

Berra, M. ;

Pastore, T. ;

Ormellese, M. .

CONSTRUCTION AND BUILDING MATERIALS, 2013, 49 :720-728

[6]

Feng Naiqian, 2004, HIGH PERFORMANCE CON, P267

[7]

Guo Li, 2011, DURABLE REHABILITATI, V4, P6

[8] Accelerated and outdoor/natural exposure testing of coatings [J].

Jacques, LFE .

PROGRESS IN POLYMER SCIENCE, 2000, 25 (09) :1337-1362

[9]

Lei Chen, 2013, NEW BUILD MAT, V11, P40

[10]

Li Guo, 2013, J XUZHOU I TECHNOL N, V28, P62

← 1 2 3 →