Measurements of Solidus and Liquidus Temperatures of CaO-Al2O3-SiO2 and CaO-MgO-Al2O3-SiO2 Slags with MnO Additions

被引：5

作者：

Wang, Lijun ^{[1
]}

Taniguchi, Yoshinori ^{[2
]}

Seetharaman, Seshadri ^{[3
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China

[2] Nippon Steel Corp Ltd, Bunkyo Ku, Tokyo, Japan

[3] Royal Inst Technol, Div Mat Proc Sci, SE-10044 Stockholm, Sweden

来源：

STEEL RESEARCH INTERNATIONAL | 2012年 / 83卷 / 02期

基金：

中国博士后科学基金;

关键词：

solidus temperature; liquidus temperature; X-ray radiography; DSC;

D O I：

10.1002/srin.201100191

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The present work was carried out with a view to re-examine the phase diagram aspects of CaO?Al2O3?SiO2 and CaO?MgO?Al2O3?SiO2 slags with MnO additions. The aim was to confirm the homogeneous liquid range necessitated for sulfide capacities measurements of the above-mentioned slags. The liquidus and solidus temperatures of these slags were measured by DSC and X-ray radiograph techniques. The experimental results were compared with the liquidus and solidus temperatures obtained from literature (Slag Atlas) and commercial softwares ThermoCalc and FactSage. The results indicate that there is good agreement between the experimental values and those retrieved from literature and the commercial software in the case of the ternary system CaO?Al2O3?SiO2. For the CaO?MgO?MnO?Al2O3?SiO2 system, significant deviations were observed between the different sources. The present observations indicate that X-ray radiography can be a very useful tool in estimating the solidus temperatures of slags while DSC would complement the information with respect to liquidus temperatures.

引用

页码：157 / 161

页数：5

共 6 条

[1]

Eisenhuttenleute V. D., 1995, SLAG ATLAS, P183

[2] LIQUIDUS TEMPERATURE AND ELECTRICAL CONDUCTIVITIES OF SYNTHETIC FERROMANGANESE SLAGS [J].

ERIC, RH ;

HEJJA, AA ;

STANGE, W .

MINERALS ENGINEERING, 1991, 4 (12) :1315-1332

[3]

Jung I. H., 1976, FACTSAGE 6 0

[4] Some Investigations into the Dynamic Mass Transfer at the Slag-Metal Interface Using Sulfur: Concept of Interfacial Velocity [J].

Muhmood, Luckman ;

Viswanathan, Nurni N. ;

Seetharaman, Seshadri .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (03) :460-470

[5]

*ROYAL I TECHN, THERM

[6]

Yoshiki B., 1952, GLASS IND, V33, P354

← 1 →