Highly enhanced dielectric strength and energy storage density in hydantoin@BaTiO3-P(VDF-HFP) composites with a sandwich-structure

被引：58
作者：
Luo, Hang [1 ]
Zhang, Dou [1 ]
Wang, Lu [1 ]
Chen, Chao [1 ]
Zhou, Jing [2 ]
Zhou, Kechao [1 ]
机构：
[1] Cent S Univ, State Key Lab Powder Met, Changsha 410083, Hunan, Peoples R China
[2] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China
来源：
RSC ADVANCES | 2015年 / 5卷 / 65期
基金：
中国国家自然科学基金;
关键词：
FERROELECTRIC POLYMER NANOCOMPOSITES; RAFT POLYMERIZATION; POLY(VINYLIDENE FLUORIDE); CONSTANT; NANODIELECTRICS; CAPACITORS; NANOWIRES; ROUTE;
D O I：
10.1039/c5ra05748e
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
A sandwich-structured composite consisted of a pure poly(vinylidene fluoride-co-hexafluoropropylene) (P(VDF-HFP)) central layer and two BaTiO3-P(VDF-HFP) neighboring layers was developed for high energy storage density. The sandwiched structure effectively enhanced dielectric properties and energy storage capacity of the composites. Breakdown strength and energy storage density of the composite with 35 vol% P(VDF-HFP) central layer reached 315 kV mm(-1) and 5.22 J cm(-3), which were enhanced by 68% and 125% compared to 187 kV mm(-1) and 2.32 J cm(-3) of the single layer composite, respectively. The dielectric constant of the composites with sandwich-structure was approximately 3 times higher than the pure P(VDF-HFP) and the dielectric loss was as low as 0.026 at 1 kHz. These results demonstrated that the sandwich-structured ceramics/polymer composite was an effective way to produce high energy density composites.
引用
收藏
页码：52809 / 52816
页数：8
相关论文
共 41 条
[1]   The barrier effect in three-layer solid dielectrics in quasi-uniform electric field [J].
Agoris, DP ;
Vitellas, I ;
Gefle, OS ;
Lebedev, SM ;
Pokholkov, YP .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2001, 34 (24) :3485-3491
[2]   Improved performances of polymer-based dielectric by using inorganic/organic core-shell nanoparticles [J].
Benhadjala, W. ;
Bord-Majek, I. ;
Bechou, L. ;
Suhir, E. ;
Buet, M. ;
Rouge, F. ;
Gaud, V. ;
Plano, B. ;
Ousten, Y. .
APPLIED PHYSICS LETTERS, 2012, 101 (14)
[3]   A dielectric polymer with high electric energy density and fast discharge speed [J].
Chu, Baojin ;
Zhou, Xin ;
Ren, Kailiang ;
Neese, Bret ;
Lin, Minren ;
Wang, Qing ;
Bauer, F. ;
Zhang, Q. M. .
SCIENCE, 2006, 313 (5785) :334-336
[4]   Influence of silane coupling agent on morphology and dielectric property in BaTiO3/polyvinylidene fluoride composites [J].
Dang, Zhi-Min ;
Wang, Hai-Yan ;
Xu, Hai-Ping .
APPLIED PHYSICS LETTERS, 2006, 89 (11)
[5]   Substantial Recoverable Energy Storage in Percolative Metallic Aluminum-Polypropylene Nanocomposites [J].
Fredin, Lisa A. ;
Li, Zhong ;
Lanagan, Michael T. ;
Ratner, Mark A. ;
Marks, Tobin J. .
ADVANCED FUNCTIONAL MATERIALS, 2013, 23 (28) :3560-3569
[6]   Improved Energy Storage Performance and Fatigue Endurance of Sr-Doped PbZrO3 Antiferroelectric Thin Films [J].
Hao, Xihong ;
Zhai, Jiwei ;
Yao, Xi .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2009, 92 (05) :1133-1135
[7]   Topological-Structure Modulated Polymer Nanocomposites Exhibiting Highly Enhanced Dielectric Strength and Energy Density [J].
Hu, Penghao ;
Shen, Yang ;
Guan, Yuhan ;
Zhang, Xuehui ;
Lin, Yuanhua ;
Zhang, Qiming ;
Nan, Ce-Wen .
ADVANCED FUNCTIONAL MATERIALS, 2014, 24 (21) :3172-3178
[8]   Highly enhanced energy density induced by hetero-interface in sandwich-structured polymer nanocomposites [J].
Hu, Penghao ;
Wang, Jianjun ;
Shen, Yang ;
Guan, Yuhan ;
Lin, Yuanhua ;
Nan, Ce-Wen .
JOURNAL OF MATERIALS CHEMISTRY A, 2013, 1 (39) :12321-12326
[9]   Largely enhanced energy density in flexible P(VDF-TrFE) nanocomposites by surface-modified electrospun BaSrTiO3 fibers [J].
Hu, Penghao ;
Song, Yu ;
Liu, Haiyang ;
Shen, Yang ;
Lin, Yuanhua ;
Nan, Ce-Wen .
JOURNAL OF MATERIALS CHEMISTRY A, 2013, 1 (05) :1688-1693
[10]   Core-Shell Structured High-k Polymer Nanocomposites for Energy Storage and Dielectric Applications [J].
Huang, Xingyi ;
Jiang, Pingkai .
ADVANCED MATERIALS, 2015, 27 (03) :546-554
12345