Measurements of friction during hot rolling of aluminum strips

被引:34
作者
Hum, B
Colquhoun, HW
Lenard, JG
机构
[1] Department of Mechanical Engineering, University of Waterloo, Waterloo
基金
加拿大自然科学与工程研究理事会;
关键词
tribology; hot rolling; aluminum;
D O I
10.1016/0924-0136(96)02350-3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In order to establish the dependence of the coefficient of friction on rolling speed and the reduction, commercially pure aluminum strips were rolled at 500 degrees C, using a 2% oil/water emulsion as the lubricant. The roll separating forces, roll torques, the forward slip, the roll pressure and the interfacial shear stress were measured as a function of the reduction and the rolling speed. The coefficient of friction was determined from the shear stress and the roll pressure distributions and its magnitude was validated independently. The coefficient of friction was found to increase with reduction and, in general, decrease with rolling speed. The adhesion theory of friction has been used to explain the observations.
引用
收藏
页码:331 / 338
页数:8
相关论文
共 14 条
[1]   EXPERIMENTAL DETERMINATION OF ROLL PRESSURE DISTRIBUTIONS IN COLD ROLLING [J].
ALSALEHI, FA ;
FIRBANK, TC ;
LANCASTER, PR .
INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 1973, 15 (09) :693-+
[2]  
BUGINI A, 1978, TRANCIATURA STAMPAGG, V15, P103
[3]  
FORD H, 1951, J ISI, V5, P57
[4]  
JANUSZKIEWICZ KR, 1995, J SOC TRIB LUB ENG, P669
[5]  
JARL M, 1988, SCAND J METALL, V17, P2
[6]  
KARAGIOZIS AN, 1985, P EUROTRIB 85 LYONS
[7]  
Koves E, 1984, ALUMINIUM KEZIKONYV
[8]  
LANG G, 1984, ALUMINUM, V60, P813
[9]   FRICTION AND FORWARD SLIP IN COLD STRIP ROLLING [J].
LENARD, JG .
TRIBOLOGY TRANSACTIONS, 1992, 35 (03) :423-428
[10]   MEASUREMENTS OF FRICTION DURING THE WARM ROLLING OF ALUMINUM [J].
LENARD, JG ;
MALINOWSKI, Z .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1993, 39 (3-4) :357-371