Mg3Si4O10(OH)2 and MgFe2O4 in situ grown on diatomite: Highly efficient adsorbents for the removal of Cr(VI)

被引：30
作者：
Du, Yucheng [1 ]
Wang, Xuekai [1 ]
Wu, Junshu [1 ]
Wang, Jinshu [1 ]
Li, Yang [1 ]
Dai, Hongxing [2 ]
机构：
[1] Beijing Univ Technol, Coll Mat Sci & Engn, Key Lab Adv Funct Mat, Minist Educ, Beijing 100124, Peoples R China
[2] Beijing Univ Technol, Dept Chem & Chem Engn, Coll Environm & Energy Engn,Lab Catalysis Chem &, Beijing Key Lab Green Catalysis & Separat,Key Lab, Beijing 100124, Peoples R China
来源：
MICROPOROUS AND MESOPOROUS MATERIALS | 2018年 / 271卷
基金：
北京市自然科学基金; 国家重点研发计划;
关键词：
Diatomite; Magnesium silicate; Magnesium ferrate; Cr(VI) removal; LAYERED DOUBLE HYDROXIDES; AQUEOUS-SOLUTION; PHOTOCATALYTIC REDUCTION; ADSORPTION CAPACITY; FACILE SYNTHESIS; SPHERES; MICROSPHERES; ABSORBENTS; CHEMISTRY; CARBON;
D O I：
10.1016/j.micromeso.2018.04.036
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Diatomite is a kind of nonmetallic mineral that possesses ordered micro- and mesoporous structures, and is well substrate materials for loading highly active oxide nanostructures for the removal of heavy metal ions. In this work, the Mg3Si4O10(OH)(2) and MgFe2O4 nanosheets were loaded on diatomite via a facile hydrothermal method. The Mg3Si4O10(OH)(2)/diatomite sample had a specific surface area of 149 m(2)/g and an extremely large adsorption capacity of 535 mg/g for Cr(VI) adsorption at room temperature, and the MgFe2O4/diatomite sample possessed a higher surface area of 335 m(2)/g and a larger capacity of 570 mg/g for Cr(VI) adsorption under UV light irradiation. The Cr(VI) adsorbed on the surface of MgFe2O4/diatomite was reduced to the less toxic Cr(III). The synergistic effect of between adsorption and photocatalysis might be the main reasons why the MgFe2O4/diatomite sample was superior to the Mg3Si4O10(OH)(2)/diatomite sample in Cr(VI) removal capacity and efficiency. It is assured that such adsorbents have a great potential for practical applications in the removal of heavy metal ions in wastewater.
引用
收藏
页码：83 / 91
页数：9
相关论文
共 39 条
[1]   Investigation of the optical properties of Mg(OH)2 and MgO nanostructures obtained by microwave-assisted methods [J].
Al-Gaashani, R. ;
Radiman, S. ;
Al-Douri, Y. ;
Tabet, N. ;
Daud, A. R. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 521 :71-76
[2]   Synthesis of ordered arrays of magnesium hydroxide nanoparticles via a simple method [J].
An, Dongmin ;
Ding, Xuefeng ;
Wang, Zichen ;
Liu, Yanhua .
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2010, 356 (1-3) :28-31
[3]   Sulfuric acid doped poly diaminopyridine/graphene composite to remove high concentration of toxic Cr(VI) [J].
Dinda, Diptiman ;
Saha, Shyamal Kumar .
JOURNAL OF HAZARDOUS MATERIALS, 2015, 291 :93-101
[4]   Flower-, wire-, and sheet-like MnO2-deposited diatomites: Highly efficient absorbents for the removal of Cr(VI) [J].
Du, Yucheng ;
Wang, Liping ;
Wang, Jinshu ;
Zheng, Guangwei ;
Wu, Junshu ;
Dai, Hongxing .
JOURNAL OF ENVIRONMENTAL SCIENCES, 2015, 29 :71-81
[5]   α-Fe2O3 nanowires deposited diatomite: highly efficient absorbents for the removal of arsenic [J].
Du, Yucheng ;
Fan, Haiguang ;
Wang, Liping ;
Wang, Jinshu ;
Wu, Junshu ;
Dai, Hongxing .
JOURNAL OF MATERIALS CHEMISTRY A, 2013, 1 (26) :7729-7737
[6]   Fabrication and excellent conductive performance of antimony-doped tin oxide-coated diatomite with porous structure [J].
Du, Yucheng ;
Yan, Jing ;
Meng, Qi ;
Wang, Jinshu ;
Dai, Hongxing .
MATERIALS CHEMISTRY AND PHYSICS, 2012, 133 (2-3) :907-912
[7]   Improved performance of surface functionalized TiO2/activated carbon for adsorption-photocatalytic reduction of Cr(VI) in aqueous solution [J].
Fu, Xiaofei ;
Yang, Hanpei ;
Lu, Guanghua ;
Tu, Yanmei ;
Wu, Junming .
MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING, 2015, 39 :362-370
[8]   Studies on the surface modification of diatomite with polyethyleneimine and trapping effect of the modified diatomite for phenol [J].
Gao, BJ ;
Jiang, PF ;
An, FQ ;
Zhao, SY ;
Ge, Z .
APPLIED SURFACE SCIENCE, 2005, 250 (1-4) :273-279
[9]   Hierarchical iron containing γ-MnO2 hollow microspheres: A facile one-step synthesis and effective removal of As(III) via oxidation and adsorption [J].
Ge, Xiao ;
Liu, Juntao ;
Song, Xiangyang ;
Wang, Guozhong ;
Zhang, Haimin ;
Zhang, Yunxia ;
Zhao, Huijun .
CHEMICAL ENGINEERING JOURNAL, 2016, 301 :139-148
[10]   Elaboration and characterisation of new mesoporous materials from diatomite and charcoal [J].
Hadjar, H. ;
Hamdi, B. ;
Jaber, M. ;
Brendie, J. ;
Kessaissia, Z. ;
Balard, H. ;
Donnet, J. B. .
MICROPOROUS AND MESOPOROUS MATERIALS, 2008, 107 (03) :219-226
1234