CTOA levels of welded joint in API X70 pipe steel

被引：16
|
作者：
Hashemi, S. H. [1 ]
Sedghi, S. [1 ]
Soleymani, V. [1 ]
Mohammadyani, D. [2 ]
机构：
[1] Univ Birjand, Dept Mech Engn, Birjand, Iran
[2] MERC, Tehran, Iran
来源：
ENGINEERING FRACTURE MECHANICS | 2012年 / 82卷
关键词：
CTOA; API X70 steel; Fracture morphology; Spiral seam weld; Ductile fracture; TIP-OPENING ANGLE; DYNAMIC FRACTURE; PROPAGATION; SPECIMEN;
D O I：
10.1016/j.engfracmech.2011.11.022
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The CTOA toughness and fracture morphology of growing crack in spirally welded steel pipe of grade API X70 were investigated. An optical test procedure based on modified double cantilever beam was used which produced a measure of the steady-state ductile fracture toughness for test material. From this, CTOA value of 8.2 degrees and 7.5 degrees were obtained for base and weld metal, respectively. The specimens fracture surfaces were examined next, which demonstrated dimple-typed shear mode fracture. Discussion on the difficulties in establishing measures of fracture resistance in pipeline steels and potential advantages and limitations of the applied test technique conclude the paper. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：46 / 59
页数：14
相关论文
共 50 条
  • [1] Effects of microstructure alteration on corrosion behavior of welded joint in API X70 pipeline steel
    Bordbar, Sajjad
    Alizadeh, Mostafa
    Hashemi, Sayyed Hojjat
    MATERIALS & DESIGN, 2013, 45 : 597 - 604
  • [2] Corrosion Behavior and Microstructural Characterization of Friction Stir Welded API X70 Steel
    Giarola, J. M.
    Calderon-Hernandez, J. W.
    Conde, F. F.
    Marcomini, J. B.
    de Melo, H. G.
    Avila, J. A.
    Bose Filho, W. W.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (08) : 5953 - 5961
  • [3] Effect of Heat Treatments on the Mechanical and Microstructure Properties of Welded API X70 Steel
    Haissam, Aboubaker
    Benarrache, Souad
    Rahmani, Rabeh Kouider
    Mansouri, Tahar
    Benhorma, Mohmmed Elhadi
    ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 2024, 48 (04): : 551 - 557
  • [4] A comprehensive study on the microstructure and mechanical properties of arc girth welded joints of spiral welded high strength API X70 steel pipe
    M. St. Węglowski
    S. Dymek
    M. Kopyściański
    J. Niagaj
    J. Rykała
    W. De Waele
    S. Hertelé
    Archives of Civil and Mechanical Engineering, 20
  • [5] A comprehensive study on the microstructure and mechanical properties of arc girth welded joints of spiral welded high strength API X70 steel pipe
    Weglowski, M. St.
    Dymek, S.
    Kopyscianski, M.
    Niagaj, J.
    Rykala, J.
    De Waele, W.
    Hertele, S.
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2020, 20 (01)
  • [6] Corrosion Behavior and Microstructural Characterization of Friction Stir Welded API X70 Steel
    J. M. Giarola
    J. W. Calderón-Hernández
    F. F. Conde
    J. B. Marcomini
    H. G. de Melo
    J. A. Avila
    W. W. Bose Filho
    Journal of Materials Engineering and Performance, 2021, 30 : 5953 - 5961
  • [7] Fatigue Behavior of Welded API 5L X70 Steel Used in Pipelines
    Şermin Özlem Turhan
    Ali Motameni
    Rıza Gürbüz
    Journal of Failure Analysis and Prevention, 2020, 20 : 1554 - 1567
  • [8] Stress Corrosion Cracking of Welded API X70 Pipeline Steel in Simulated Underground Water
    Z. Y. Liu
    C. W. Du
    C. Li
    F. M. Wang
    X. G. Li
    Journal of Materials Engineering and Performance, 2013, 22 : 2550 - 2556
  • [9] Fatigue Behavior of Welded API 5L X70 Steel Used in Pipelines
    Turhan, Sermin Ozlem
    Motameni, Ali
    Gurbuz, Riza
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2020, 20 (05) : 1554 - 1567
  • [10] Stress Corrosion Cracking of Welded API X70 Pipeline Steel in Simulated Underground Water
    Liu, Z. Y.
    Du, C. W.
    Li, C.
    Wang, F. M.
    Li, X. G.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (09) : 2550 - 2556
12345