Numerical simulation and validation of subsurface modification and crack formation induced by nanosecond-pulsed laser processing in monocrystalline silicon

被引:18
作者
Kiyota, H. [1 ,2 ]
Hara, K. [2 ]
Jankowski, M. [1 ]
Fejer, M. M. [1 ]
机构
[1] Stanford Univ, Edward L Ginzton Lab, Stanford, CA 94305 USA
[2] Hamamatsu Photon KK, Electron Tube Div, Iwata, Shizuoka 4380193, Japan
关键词
TEMPERATURE; INDENTATION; DEPENDENCE; CRYSTALS; FRACTURE; DENSITY;
D O I
10.1063/1.5130701
中图分类号
O59 [应用物理学];
学科分类号
摘要
We describe a numerical simulation of subsurface modification and crack formation in monocrystalline silicon induced by nanosecondpulsed laser irradiation. In this model, we assume the residual stress generation due to material transfer caused by volume reduction during melting and resolidification to be the dominant factor in creating subsurface mechanical stress and cracks. In order to quantitatively determine the geometry of the modified region, we numerically model the nonlinear propagation and absorption of the laser beam and the thermal transport. We find that during a single pulse, the lattice temperature distribution results in melting, material transfer, and structural changes on resolidification. The residual stress generated within the monocrystal adjacent to the modified region is subsequently assessed for crack formation in the substrate. The validity of the proposed model is confirmed through agreement with a number of experimental results, including the transmitted power, the timing of the onset of the phase transition during laser irradiation, the processing threshold, the geometry of the modified region, and the formed crack length. (C) 2020 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
引用
收藏
页数:11
相关论文
共 41 条
[1]   Two-photon absorption and Kerr coefficients of silicon for 850-2200 nm [J].
Bristow, Alan D. ;
Rotenberg, Nir ;
van Driel, Henry M. .
APPLIED PHYSICS LETTERS, 2007, 90 (19)
[2]   FRACTURE OF DIRECTIONALLY SOLIDIFIED MULTI-CRYSTALLINE SILICON [J].
CHEN, CP ;
LEIPOLD, MH ;
HELMREICH, D .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1982, 65 (04) :C49-C49
[3]   Characterization of Young's modulus of silicon versus temperature using a "beam deflection" method with a four-point bending fixture [J].
Cho, Chun-Hyung .
CURRENT APPLIED PHYSICS, 2009, 9 (02) :538-545
[4]   DENSITY OF AMORPHOUS SI [J].
CUSTER, JS ;
THOMPSON, MO ;
JACOBSON, DC ;
POATE, JM ;
ROORDA, S ;
SINKE, WC ;
SPAEPEN, F .
APPLIED PHYSICS LETTERS, 1994, 64 (04) :437-439
[5]   CARRIER MOBILITIES IN SILICON SEMI-EMPIRICALLY RELATED TO TEMPERATURE, DOPING AND INJECTION LEVEL [J].
DORKEL, JM ;
LETURCQ, P .
SOLID-STATE ELECTRONICS, 1981, 24 (09) :821-825
[6]   Calculation of the density and heat capacity of silicon by molecular dynamics simulation [J].
Endo, Rie Kojima ;
Fujihara, Yusuke ;
Susa, Masahiro .
High Temperatures - High Pressures, 2003, 35-36 (05) :505-511
[7]  
Frey B. J., 2007, P OPT TECHN ASTR
[8]  
Fujita M., 2009, P INT C APPL LAS EL
[9]  
Hooper A., 2015, P 2015 IEEE 65 EL CO, V1436
[10]  
Ino Y., 2012, KEY ENG MATER, V754, P123