Effect of oxidation processing on the surface properties and floatability of Meizhiyou long-flame coal
被引:54
作者:
Chen, Songjiang
[1
,2
]
Tang, Longfei
[1
,2
]
Tao, Xiuxiang
[1
,2
]
Chen, Liang
[2
]
Yang, Zhao
[2
]
Li, Lulu
[2
]
机构:
[1] China Univ Min & Technol, Key Lab Coal Proc & Efficient Utilizat, Minist Educ, Xuzhou 221116, Peoples R China
[2] China Univ Min & Technol, Sch Chem Engn & Technol, Xuzhou 221116, Peoples R China
来源:
基金:
中国国家自然科学基金;
关键词:
Long-flame coal;
Oxidation;
Surface chemical structure;
Surface morphology;
Hydrophobicity;
Floatability;
LOW-TEMPERATURE OXIDATION;
LOW-RANK COAL;
BITUMINOUS COAL;
FT-IR;
FLOTATION;
DESULFURIZATION;
HYDROPHOBICITY;
ATTACHMENT;
MECHANISM;
PRODUCTS;
D O I:
10.1016/j.fuel.2017.08.053
中图分类号:
TE [石油、天然气工业];
TK [能源与动力工程];
学科分类号:
0807 ;
0820 ;
摘要:
The surface properties of coal play a crucial role in its flotation, therefore it is of great significance to investigate the changes in both chemical structure and surface morphology in oxidation process of low rank coal. In this paper, the mechanism of difficult floatation of oxidized coal was highlighted. The surface hydrophobicity and floatability of Meizhiyou long-flame coal before and after oxidation processing with H2O2 solution at different concentration were evaluated by induction time and contact angle analyses as well as flotation tests, while the changes in its surface properties in the oxidation process were analyzed by XPS, FTIR, BET and SEM measurements. The maximum increase extent of induction time between bubbles and oxidized coal particles reached to 13217% while the maximum reduction extent of combustible matter recovery reached to 95.28%, which indicated the floatability of oxidized coal particles almost decreased exponentially along with the increase of concentration of H2O2 solution. Additionally, the results suggested the active chemical functional groups of > CH2 peak at 1437 cm(-1), -CH3 peak at 1373 cm(-1) and C-O-C peak at 1215 cm(-1) were susceptible to oxidation. After oxidation processing, on the one hand, the content of hydrophobic groups on coa(l) surface showed an obvious decrease while that of hydrophilic groups showed a significant increase. What's more, the content of carbonyl group had a close correlation with the extent of oxidation of the coal sample. On the other hand, it was found that the surface morphology of coals was significantly changed after oxidation process, and there were more pores and cracks on the coal surface. As a result, the contact angle of coals showed a significant decline after oxidation processing and it declined more quickly with the increase of contact time. Consequently, the poor flotation performance of oxidized coals may be attributed to the dramatic changes in both surface chemical structure and surface morphology in oxidation process.