Cure Kinetics of Poly(acrylonitrile-butadiene-styrene) Modified Epoxy-Amine System

The cure kinetics of epoxy based on the diglycidyl ether of bisphenol A (DGEBA) modified with different amounts of poly(acrylonitrile-butadiene-styrene) (ABS) and cured with 4,4'-diaminodiphenylsulfone (DDS) was investigated by employing differential scanning calorimetry (DSC). The curing reaction was followed by using an isothermal approach over the temperature range 150-180 degrees C. The amount of ABS in the blends was 3.6, 6.9, 10 and 12.9 wt%. Blending of ABS in the epoxy monomer did not change the reaction mechanism of the epoxy network formation, but the reaction rate seems to be decreased with the addition of the thermoplastic. A phenomenological kinetic model was used for kinetic analysis. Activation energies and kinetic parameters were determined by fitting the kinetic model with experimental data. Diffusion control was incorporated to describe the cure in the latter stages, predicting the cure kinetics over the whole range of conversion. The reaction rates for the epoxy blends were found to be lower than that of the neat epoxy. The reaction rates decreased when the ABS contents was increased, due to the dilution effect caused by the ABS on the epoxy/amine reaction mixture.