Influence of Calcium Bentonite Addition on the Compressive Strength, Efflorescence Extent and Drying Shrinkage of Fly-Ash Based Geopolymer Mortar

被引：18
作者：
Huang, Yi [1 ]
机构：
[1] Hunan City Univ, Sch Mat & Chem Engn, Yiyang 413002, Peoples R China
来源：
TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY | 2020年 / 79卷 / 02期
关键词：
Geopolymer; Calcium bentonite; Compressive strength; Efflorescence; Drying shrinkage; MECHANICAL-PROPERTIES; MICROSTRUCTURE; LIMESTONE; BEHAVIOR; ZEOLITE;
D O I：
10.1080/0371750X.2020.1719206
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The influence of calcium bentonite addition on the compressive strength, efflorescence extent and drying shrinkage of fly-ash based geopolymer mortar was investigated. The results showed that appropriate amount (e.g. 15 wt%) of calcium bentonite addition favoured the enhancement of compressive strength mainly because its addition allowed the geopolymer to tolerate more water glass addition and therefore increased the Si/Al ratio of geopolymer. The maximum 28 d compressive strength of the geopolymer mortar with calcium bentonite addition reached 47.8 MPa, which was evidently larger than the maximum value of the specimen without calcium bentonite addition. Calcium bentonite addition was also beneficial for the reduction of drying shrinkage percentage of geopolymer mortar due to water adsorption and volume expansion properties of calcium bentonite. Moreover, calcium bentonite addition could reduce, even eliminate the efflorescence mainly due to Na+ adsorption by calcium bentonite through ion exchange.
引用
收藏
页码：77 / 82
页数：6
相关论文
共 30 条
  • [1] Afshan A., 2014, MATER SCI FORUM, V803, P355, DOI [10.4028/www.scientific.net/MSF.803.355, DOI 10.4028/WWW.SCIENTIFIC.NET/MSF.803.355]
  • [2] [曹灿 Cao Can], 2013, [地学前缘, Earth Science Frontiers], V20, P220
  • [3] [曹吉林 Cao Jilin], 2002, [过程工程学报, The chinese journal of process engineering], V2, P204
  • [4] [陈宝 Chen Bao], 2013, [岩土工程学报, Chinese Journal of Geotechnical Engineering], V35, P181
  • [5] The effect of limestone on sodium hydroxide-activated metakaolin-based geopolymers
    Cwirzen, Andrzej
    Provis, John L.
    Penttala, Vesa
    Habermehl-Cwirzen, Karin
    [J]. CONSTRUCTION AND BUILDING MATERIALS, 2014, 66 : 53 - 62
  • [6] GEOPOLYMERS - INORGANIC POLYMERIC NEW MATERIALS
    DAVIDOVITS, J
    [J]. JOURNAL OF THERMAL ANALYSIS, 1991, 37 (08): : 1633 - 1656
  • [7] Effects of adding nano-TiO2 on compressive strength, drying shrinkage, carbonation and microstructure of fluidized bed fly ash based geopolymer paste
    Duan, Ping
    Yan, Chunjie
    Luo, Wenjun
    Zhou, Wei
    [J]. CONSTRUCTION AND BUILDING MATERIALS, 2016, 106 : 115 - 125
  • [8] Ultrasound enhanced geopolymerisation
    Feng, D
    Tan, H
    Van Deventer, JSJ
    [J]. JOURNAL OF MATERIALS SCIENCE, 2004, 39 (02) : 571 - 580
  • [9] Properties of alkali activated slag-fly ash blends with limestone addition
    Gao, X.
    Yu, Q. L.
    Brouwers, H. J. H.
    [J]. CEMENT & CONCRETE COMPOSITES, 2015, 59 : 119 - 128
  • [10] Bentonite transformations in strongly alkaline solutions
    Gates, W. P.
    Bouazza, A.
    [J]. GEOTEXTILES AND GEOMEMBRANES, 2010, 28 (02) : 219 - 225
123