Results of Investigations of 500 kg Nb3Sn Bronze Strand Produced in Russian Federation for ITER Project

被引:4
作者
Abdyukhanov, I. M. [1 ]
Shikov, A. K. [2 ]
Vorobyeva, A. E. [1 ]
Pantsyrnyy, V. I. [1 ]
Beliakov, N. A. [1 ]
Dergunova, E. A. [1 ]
Mareev, K. A. [1 ]
Nasibulin, M. N. [1 ]
Zernov, S. M. [3 ]
Abramushin, K. M. [4 ]
Anishuk, D. S. [4 ]
机构
[1] Bochvar Inst Inorgan Mat VNIINM, Moscow 123098, Russia
[2] RRC Kurchatov Inst, Moscow 123182, Russia
[3] JSC TVEL, Moscow 115409, Russia
[4] JSC Chepetsky Mech Plant JSC ChMP, Glasov 427620, Russia
关键词
ITER; Nb3Sn; strand;
D O I
10.1109/TASC.2010.2103547
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
The results of investigations of first 500 kg Nb3Sn bronze strand are presented. This batch of strands was meant for the production of 100 m of Toroidal Field Conductor in the frame of fulfillment the Phase II of Procurement Arrangement between Russian Domestic Agency and International Organization ITER. In order to provide the industrial-scale production of strands design documentation and all necessary quality assurance documents were developed. The developed industrial technology of Nb3Sn strand production was applied in Joint Stock Company << Chepetsky Mechanical Plant >> (JSC << ChMP >>). Strands were produced in JSC << ChMP >> from final billets with diameter of 203 mm. The microstructure investigations of produced strands were performed before and after diffusion annealing by optical microscopy, X-ray microprobe analysis. Mechanical properties of annealed Nb3Sn strands were investigated. Current-carrying capability of Nb3Sn strands at 12 T, 4.22 K were studied. It was shown, that all produced strands met all the requirements, in particular I-c was from 202 to 220 A; hysteresis losses were from 165 to 194 mJ/cm(3) (+/- 3 T).
引用
收藏
页码:2567 / 2570
页数:4
相关论文
共 4 条
[1]  
Jewell M. C., 2010, IEEE T APPL SUPERCON, V20
[2]   Microstructure and properties of Nb3Sn superconductors for the magnet system of the international thermonuclear experimental reactor [J].
Shikov, AK ;
Panstsyrnyi, VI ;
Vorob'eva, AV ;
Dergunova, EA ;
Sud'ev, SV ;
Mareev, KA ;
Belyakov, NA ;
Abdyukhanov, IM ;
Sergeev, VV .
METAL SCIENCE AND HEAT TREATMENT, 2004, 46 (11-12) :504-513
[3]  
Vasilyev R., ASC 2010
[4]   Development and research of the Nb3Sn superconductor with improved structure of superconductive layer [J].
Vorobieva, AE ;
Shikov, AK ;
Pantsyrny, VI ;
Dergunova, EA ;
Mareev, KA ;
Farafonov, DA ;
Vojdaev, LI ;
Lomaev, VM .
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) :3407-3409