XPS characterization and corrosion resistance of cerium-treated magnesium coatings

被引:19
作者
Ben Hassen, Samia [1 ,3 ]
Bousselmi, Latifa [2 ]
Bercot, Patrice [3 ]
Rezrazi, El Mustafa [3 ]
Triki, Ezzeddine [1 ]
机构
[1] ENIT, Unite Rech Corros & Protect Metall, Tunis, Tunisia
[2] CERTE, Lab Traitement & Recyclage Eaux, Borj Cedria, Tunisia
[3] Univ Franche Comte, CNRS UMR 6213, Inst UTINAM, F-25030 Besancon, France
关键词
cerium compounds; magnesium; coatings; X-ray photoelectron spectroscopy; corrosion resistance; CONVERSION COATINGS; AQUEOUS SYSTEMS; PHASE-STABILITY; PROTECTION; FILMS; SPECTROSCOPY; DIAGRAM; ALLOY; OXIDE;
D O I
10.1007/s12598-011-0398-y
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Cerium conversion treatment was applied on magnesium coatings in a solution containing CeCl3. The composition of the cerium conversion layer on magnesium was investigated using X-ray photoelectron spectroscopy (XPS). It was revealed that the composition predominately consisted of a three-valent state cerium compound with a relative abundance around 90%. Some of Ce3+ was oxidized to Ce4+. Electrochemical impedance spectroscopy results revealed that the total impedance of cerium-treated samples increased for a short immersion time in NaCl solution before coating deteriorating. This deterioration was due to the coating porosity increasing and the breakdown of the conversion layer.
引用
收藏
页码:368 / 373
页数:6
相关论文
共 22 条
[1]   Studies of the formation of cerium-rich protective films using x-ray absorption near-edge spectroscopy and rotating disk electrode methods [J].
Aldykiewicz, AJ ;
Davenport, AJ ;
Isaacs, HS .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1996, 143 (01) :147-154
[2]   Comparison of testing solutions on the protection of Al-alloys using a Mg-rich primer [J].
Battocchi, D. ;
Simoes, A. M. ;
Tallman, D. E. ;
Bierwagen, G. P. .
CORROSION SCIENCE, 2006, 48 (08) :2226-2240
[3]   Electrochemical behaviour of a Mg-rich primer in the protection of Al alloys [J].
Battocchi, D. ;
Simoes, A. M. ;
Tallman, D. E. ;
Bierwagen, G. P. .
CORROSION SCIENCE, 2006, 48 (05) :1292-1306
[4]   Kinetic and mechanistic studies of rare earth-rich protective film formation using in situ ellipsometry [J].
Böhm, S ;
Greef, R ;
McMurray, HN ;
Powell, SM ;
Worsley, DA .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2000, 147 (09) :3286-3293
[5]   Effect of HCl pre-treatment on corrosion resistance of cerium-based conversion coatings on magnesium and magnesium alloys [J].
Brunelli, K ;
Dabalà, M ;
Calliari, I ;
Magrini, M .
CORROSION SCIENCE, 2005, 47 (04) :989-1000
[6]   Formation of a cerium-based conversion coating on AA2024: relationship with the microstructure [J].
Campestrini, P ;
Terryn, H ;
Hovestad, A ;
de Wit, JHW .
SURFACE & COATINGS TECHNOLOGY, 2004, 176 (03) :365-381
[7]   Cerium-based chemical conversion coating on AZ63 magnesium alloy [J].
Dabalà, M ;
Brunelli, K ;
Napolitani, E ;
Magrini, M .
SURFACE & COATINGS TECHNOLOGY, 2003, 172 (2-3) :227-232
[8]   XANES INVESTIGATION OF THE ROLE OF CERIUM COMPOUNDS AS CORROSION-INHIBITORS FOR ALUMINUM [J].
DAVENPORT, AJ ;
ISAACS, HS ;
KENDIG, MW .
CORROSION SCIENCE, 1991, 32 (5-6) :653-663
[9]   Study of the deposition of cerium oxide by conversion on to aluminium alloys [J].
Decroly, A ;
Petitjean, JP .
SURFACE & COATINGS TECHNOLOGY, 2005, 194 (01) :1-9
[10]  
Hassen S.Ben., 2008, Surf. Coat. Tech, V202, P3579