Magnetic properties of extremely small Nd-Fe-B sintered magnets

被引：305

作者：

Nakamura, H ^{[1
]}

Hirota, K ^{[1
]}

Shimao, M ^{[1
]}

Minowa, T ^{[1
]}

Honshima, M ^{[1
]}

机构：

[1] Shin Etsu Chem Co Ltd, Magnet Mat Res Ctr, Takefu 9158515, Japan

来源：

IEEE TRANSACTIONS ON MAGNETICS | 2005年 / 41卷 / 10期

关键词：

Dy2O3; DyF3; coercivity; grain size; surface area/volume ratio; surface diffusion; TbF3;

D O I：

10.1109/TMAG.2005.854874

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Magnetic properties of small Nd-Fe-B sintered magnets were investigated. Thickness of surface damaged layer, which shows low coercivity and causes the deterioration in magnetic properties, was found to be comparable to mean grain size of sintered bodies. Magnets with small grains of around 5 mu m showed rather higher magnetic performance after machining into small pieces with a surface area/volume ratio of 20-35 mm(-1). Chemical etching with a nitric acid solution was effective in partial recovery of magnetic properties through bringing slightly higher coercivity of surface grains. Heat treatment at higher temperatures than the melting point of Nd-rich phase and subsequent aging enhanced the coercivity of surface grains. Coating with powders of Dy-2 O-3, DyF3, or TbF3 before the heat treatment resulted in a great enhancement in coercivity without significant reduction in remanence.

引用

页码：3844 / 3846

页数：3

共 6 条

[1] Development of high coercive powder from the Nd-Fe-B sintered magnet scrap [J].

Kim, AS ;

Kim, DH ;

Namkung, S ;

Jang, TS ;

Lee, DH ;

Kwon, HW ;

Hwang, DH .

IEEE TRANSACTIONS ON MAGNETICS, 2004, 40 (04) :2877-2879

[2]

Machida K., 2004, SPRING M JAP SOC POW, P202

[3] Fabrication of Nd-Fe-B thick-film magnets by high-speed PLD method [J].

Nakano, M ;

Katoh, R ;

Fukunaga, H ;

Tutumi, S ;

Yamashita, F .

IEEE TRANSACTIONS ON MAGNETICS, 2003, 39 (05) :2863-2865

[4]

Park K.T., 2000, Proceedings of the 16th Workshop Rare-Earth Magnets and Their Applications, P257

[5]

YAMAMOTO K, 2002, P 17 INT WORKSH RAR, P648

[6] ANISOTROPIC ND-FE-B THIN-FILM MAGNETS FOR MILLI-SIZE MOTOR [J].

YAMASHITA, S ;

YAMASAKI, J ;

IKEDA, M ;

IWABUCHI, N .

JOURNAL OF APPLIED PHYSICS, 1991, 70 (10) :6627-6629

← 1 →