Synthesis of titanium dioxide/reduced graphene oxide nanocomposite by ultrasound-assisted mechanical mixing method for fabricating photoanode to upgrade the performance and stability of dye-sensitized solar cell

被引：10

作者：

Cuong, Dang Lam Tuan ^{[1
,2
,3
]}

Van Cuong, Le ^{[1
,2
,3
]}

Nghia, Le Tran Trung ^{[1
,2
,3
]}

Trinh, Dinh Ngoc ^{[1
,2
,3
]}

Linh, Nguyen Thi Thuy ^{[1
,2
,3
]}

Hai, Nguyen Duy ^{[1
,2
,3
]}

Chau, Pham Trong Liem ^{[1
,2
,3
]}

Hoang, Nguyen Thai ^{[1
,4
]}

Phong, Mai Thanh ^{[1
,2
,3
]}

Hieu, Nguyen Huu ^{[1
,2
,3
]}

机构：

[1] Ho Chi Minh City Univ Technol HCMUT, Key Lab Chem Engn & Petr Proc, Key CEPP Lab, VNU HCM, 268 Ly Thuong Kiet St, Dist 10, Ho Chi Minh City, Vietnam

[2] Ho Chi Minh City Univ Technol HCMUT, Fac Chem Engn, 268 Ly Thuong Kiet St, Dist 10, Ho Chi Minh City, Vietnam

[3] Vietnam Natl Univ Ho Chi Minh City VNU HCM, Linh Trung Ward, Ho Chi Minh City, Vietnam

[4] Univ Sci, 227 Nguyen Cu St, Dist 5, Ho Chi Minh City, Vietnam

来源：

MATERIALS RESEARCH BULLETIN | 2022年 / 156卷

关键词：

Titanium dioxide; Reduced graphene oxide; Dye-sensitized solar cell; Photostability; Thermostability; TERM THERMAL-STABILITY; ONE-STEP SYNTHESIS; PHOTOCATALYTIC DEGRADATION; RHODAMINE-B; TIO2; NANOPARTICLES; ENHANCEMENT; TEMPERATURE; EFFICIENCY; FILMS;

D O I：

10.1016/j.materresbull.2022.112000

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Herein, titanium dioxide/reduced graphene oxide (TiO2/rGO - TG) nanocomposite was synthesized via the ultrasound-assisted mechanical mixing method, used for the fabrication of photoanode in dye-sensitized solar cells (DSSCs). The DSSCs performance was evaluated by current density-voltage (J-V) curves and electrochemical impedance spectroscopy (EIS), showing that the sample with 1.0 wt.% rGO under the ultrasonic power of 720 W, was an optimal material for fabricating photoanode in DSSCs, which obtained the power conversion efficiency of 6.37%. Additionally, in the 500-h illumination test under 300-watt metal-halide lamp and the 100-h drying at 85 C, DSSCs with the presence of rGO proved better stability in comparison with DSSCs fabricated from commercial TiO2. The characterization of TG was analyzed by ultraviolet-visible spectroscopy, Fourier-transform infrared spectroscopy, Raman spectroscopy, X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy, indicating that TiO(2 )nanoparticles are uniformly distributed onto the rGO sheets with the average diameter from 20 to 70 nm.