Leaching of Ca-Rich Slags Produced from Reductive Smelting of Bauxite Residue with Na2CO3 Solutions for Alumina Extraction: Lab and Pilot Scale Experiments

Sustainable utilization of Bauxite Residue (BR) is currently one of the greatest challenges being tackled by the alumina industry, due to its high production rates and limited reuse options. The present work is concerned with the use of BR as a candidate metallurgical raw material for iron (Fe) production and aluminum (Al) extraction. In more detail, at first, BR undergoes reductive smelting to extract its Fe content and produce a slag of mainly calcium aluminate composition. In a second step, Al contained in the calcium aluminate phases is extracted hydrometallurgically by leaching with a Na2CO3 aqueous solution. The focus of the current study is the optimization of this leaching process, and it was performed in two stages. The first was a laboratory scale investigation on the main parameters affecting the extraction rate of Al. The second stage was performed in pilot scale and incorporated observations and suggestions based on the laboratory scale investigation. Laboratory work showed that more than 50% of aluminum could be easily extracted in less than 1 h, in 5% S/L, at 70 degrees C and with an 20% excess of Na2CO3. Pilot scale work, by successfully applying the suggestions derived from laboratory scale work, achieved an average Al extraction of 68% from a 10% S/L pulp, with a slag of optimized composition in relation to the one used in the laboratory scale.